Relflex Elastomers | S t r e t c h i n g L i m i t s

Tyre Application
Non-Tyre Application
Tube & Bladder

TBR INNERLINER-BIIR

Ingredient	PHR	%
BROMOBUTYL IMPRAMER B2232	100.00	55.25
CARBON GPF N660	60.00	33.15
PARAFFINIC OIL	8.00	4.42
PF RESIN	3.00	1.66
TACKIFIER MS40	5.00	2.76
STEARIC ACID	1.50	0.83
ZINC OXIDE	2.00	1.10
ACCELERATOR MBTS	1.00	0.55
SULFUR	0.50	0.28
TOTAL	181.00	100.00

Properties	Method	Typical Value
Tc90 @145°C (min)	ASTM D5289	29.0
Physical properties (cured @ 145°C/Tc90+2 min)
300% Modulus (MPa)	ASTM D412	4.0
Tensile Strength (MPa)	ASTM D412	10.8
Elongation @ Break (%)	ASTM D412	772
Hardness (Shore A)	ASTM D2240	43
Air retention properties (cured @ 145°C/Tc90+2 min)
Air permeability (cc-mm/[m2-day])	ASTM 3985	58

The information provided above is for reference purpose only. We don not guarantee, expressly or impliedly, the intended application by user. We request the user to validate the information in their plant, process, products and its intended application before implementation. Trade names, if any, used are only for information and in no way promoting the specific material. Reliance Industries Limited disclaim liability for any loss, direct or indirect injury suffered , or damage incurred as a result of above information/this document.

PCR INNERLINER

Ingredient	PHR	%
CHLOROBUTYL IMPRAMER C1139	60.00	32.02
NR (RSS4)	40.00	21.34
CARBON GPF N660	60.00	32.02
HOMOGENIZER MS40	7.00	3.74
NAPHTHENIC OIL	8.00	4.27
MAGNESIUM OXIDE	0.15	0.08
PF RESIN	4.00	2.13
ANTIOXIDANT TDQ	1.00	0.53
STEARIC ACID	2.00	1.07
ZINC OXIDE	3.00	1.60
ACCELERATOR MBTS	1.50	0.80
SULFUR	0.75	0.40
TOTAL	187.40	100.00

Properties	Method	Typical Value
Tc90 @160°C (min)	ASTM D5289	9.0
Physical Properties (Cured @ 160°C/Tc90+2 min)
300% Modulus (MPa)	ASTM D412	3.1
Tensile Strength (MPa)	ASTM D412	6.2
Elongation @ Break (%)	ASTM D412	663
Hardness (Shore A)	ASTM D2240	47
Air Retention properties (Cured @ 160°C/Tc90+2 min)
Air permeability (cc-mm/[m2-day])	ASTM D3985	169

Tyre tread -Passenger Car Radial : PCRT 1

Ingredient	PHR	%
STYLAMER SBR-1712	96.25	43.88
CISAMER-01	30.00	13.68
CARBON ISAF N220	70.00	31.91
AROMATIC OIL	12.00	5.47
ANTIOXIDANT TQ	1.00	0.46
ANTIOXIDANT 6PPD	1.50	0.68
MC WAX/WAX BLEND	2.00	0.91
ZINC OXIDE	2.50	1.14
STEARIC ACID	1.00	0.46
ACCELERATOR DPG	0.10	0.05
ACCELERATOR TBBS	1.00	0.46
SULFUR	2.00	0.91
TOTAL	219.35	100.00

Properties	Method	Typical Value
Tc90 @160°C (min)	ASTM D5289	14.0
Physical Properties (Cured @160°C/Tc90+2 min)
300% Modulus (MPa)	ASTM D412	6.4
Tensile Strength (MPa)	ASTM D412	20.2
Elongation @ Break (%)	ASTM D412	651
Hardness (Shore A)	ASTM D2240	55
Abrasion Properties (Cured @160°C/Tc90+5 min)
Abrasion Loss (mm³)	ASTM D5963	107
Rebound Resilience (Cured @160°C/Tc90+5 Min)
Rebound Resilience @25°C (%)	ISO 4662	35
Heat Build Up Properties (Cured @160°C/Tc90+5 min)- 30 Hz, 100°C, 7 kg, 25 min
HBU (°C)	ASTM D623	30

The information provided above is for reference purpose only. We do not guarantee, expressly or impliedly, the intended application by user. We request the user to validate the information in their plant, process, products and its intended application before implementation. Trade names, if any, used are only for information and in no way promoting the specific material. Reliance Industries Limited disclaim liability for any loss, direct or indirect injury suffered , or damage incurred as a result of above information/this document.

Tyre tread -Passenger Car Radial : PCRT 2

Ingredient	PHR	%
STYLAMER SBR-1723	96.25	43.88
CISAMER-01	30.00	13.68
CARBON ISAF N220	70.00	31.91
PROCESS OIL	12.00	5.47
ANTIOXIDANT TQ	1.00	0.46
ANTIOXIDANT 6PPD	1.50	0.68
MC WAX/ WAX BLEND	2.00	0.91
STEARIC ACID	1.00	0.46
ZINC OXIDE	2.50	1.14
ACCELERATOR DPG	0.10	0.05
ACCELERATOR TBBS	1.00	0.46
SULFUR	2.00	0.91
TOTAL	219.35	100.00

Properties	Method	Typical Value
Tc90 @160°C (min)	ASTM D5289	12.0
Physical Properties (Cured @160°C/Tc90+2 min)
300% Modulus (MPa)	ASTM D412	6.5
Tensile Strength (MPa)	ASTM D412	18.0
Elongation @ Break (%)	ASTM D412	616
Hardness (Shore A)	ASTM D2240	54
Abrasion Properties (Cured @160°C/Tc90+5 min)
Abrasion Loss (mm³)	ASTM D5963	85
Rebound Resilience (Cured @160°C/Tc90+5 Min)
Rebound Resilience @25°C (%)	ISO 4662	38
Heat Build Up Properties (Cured @160°C/Tc90+5 min)- 30 Hz, 100°C, 7 kg, 25 min
HBU (°C)	ASTM D623	23

Tyre tread -Passenger Car Radial : PCRT 3

Ingredient	PHR	%
STYLAMER SBR-1502	60.00	30.22
CISAMER-700	40.00	20.15
CARBON ISAF N220	70.00	35.26
PROCESS OIL	17.00	8.56
ANTIOXIDANT TQ	1.00	0.50
ANTIOXIDANT 6PPD	1.50	0.76
MC WAX/ WAX BLEND	2.00	1.01
STEARIC ACID	1.00	0.50
ZINC OXIDE	2.50	1.26
ACCELERATOR DPG	0.20	0.10
ACCELERATOR TBBS	1.25	0.63
SULFUR	2.00	1.01
RETARDER PVI	0.10	0.05
TOTAL	198.55	100.00

Properties	Method	Typical Value
Tc90 @160°C (min)	ASTM D5289	8.5
Physical Properties (Cured @160°C/Tc90+2 Min)
300% Modulus (MPa)	ASTM D412	12.0
Tensile Strength (MPa)	ASTM D412	20.0
Elongation @ Break (%)	ASTM D412	470
Hardness (Shore A)	ASTM D2240	68
Abrasion Properties (Cured @160°C/Tc90+5 Min)
Abrasion Loss (mm³)	ASTM D5963	89
Rebound Resilience (Cured @160°C/Tc90+5 Min)
Rebound Resilience @25°C (%)	ISO 4662	35
Heat Build Up Properties (Cured @160°C/Tc90+5 min)- 30 Hz, 100°C, 7 kg, 25 min
HBU (°C)	ASTM D623	27

TYRE TREAD -PASSENGER CAR RADIAL : PCRT 4

Ingredient	PHR	%
SSBR (21% STYRENE, 62.2 % VINYL CONTENT)	60.00	29.90
CISAMER-01	40.00	19.94
PPT SILICA VN3	65.00	32.39
SILANE COUPLING AGENT Si-69	5.85	2.92
PROCESS OIL	17.00	8.47
ANTIOXIDANT TDQ	1.00	0.50
ANTIOXIDANT 6PPD	1.50	0.75
MC WAX/ WAX BLEND	2.00	1.00
STEARIC ACID	1.00	0.50
ZINC OXIDE	2.50	1.25
ACCELERATOR TBBS	1.50	0.75
SULFUR	1.80	0.90
ACCELERATOR DPG	1.50	0.75
TOTAL	200.65	100.00

Properties	Method	Typical Value
Tc90 @160°C (min)	ASTM D5289	8.3
Physical Properties (Cured @160°C/Tc90+2 Min)
300% Modulus (MPa)	ASTM D412	10.8
Tensile Strength (MPa)	ASTM D412	18.3
Elongation @ Break (%)	ASTM D412	441
Hardness (Shore A)	ASTM D2240	67
Abrasion Properties (Cured @160°C/Tc90+5 Min)
Abrasion Loss (mm³)	ASTM D5963	92
Rebound Resilience (Cured @160°C/Tc90+5 Min)
Rebound Resilience @25°C (%)	ISO 4662	47.7
Heat Build Up Properties (Cured @160°C/Tc90+5 Min) - 30Hz, 100°C, 7kg, 25 min
HBU (°C)	ASTM D623	18

TYRE TREAD -PASSENGER CAR RADIAL : PCRT 5

Ingredient	PHR	%
SSBR (21% STYRENE, 62.2 % VINYL CONTENT)	60.00	29.90
CISAMER-1220	40.00	19.94
PPT SILICA VN3	65.00	32.39
SILANE COUPLING AGENT Si-69	5.85	2.92
PROCESS OIL	17.00	8.47
ANTIOXIDANT TDQ	1.00	0.50
ANTIOXIDANT 6PPD	1.50	0.75
MC WAX/ WAX BLEND	2.00	1.00
STEARIC ACID	1.00	0.50
ZINC OXIDE	2.50	1.25
ACCELERATOR TBBS	1.50	0.75
SULFUR	1.80	0.90
ACCELERATOR DPG	1.50	0.75
TOTAL	200.65	100.00

Properties	Method	Typical Value
Tc90 @160°C (min)	ASTM D5289	9.2
Physical Properties (Cured @160°C/Tc90+2 Min)
300% Modulus (MPa)	ASTM D412	11.8
Tensile Strength (MPa)	ASTM D412	17.3
Elongation @ Break (%)	ASTM D412	427
Hardness (Shore A)	ASTM D2240	67
Abrasion Properties (Cured @160°C/Tc90+5 Min)
Abrasion Loss (mm³)	ASTM D5963	97
Rebound Resilience (Cured @160°C/Tc90+5 Min)
Rebound Resilience @25°C (%)	ISO 4662	47.3
Heat Build Up Properties (Cured @160°C/Tc90+5 Min) - 30Hz, 100°C, 7kg, 25 min
HBU (°C)	ASTM D623	18

TYRE TREAD -PASSENGER CAR RADIAL : PCRT 6

Ingredient	PHR	%
SSBR (21% STYRENE, 62.2 % VINYL CONTENT)	60.00	29.90
CISAMER-700	40.00	19.94
PPT SILICA VN3	65.00	32.39
SILANE COUPLING AGENT Si-69	5.85	2.92
PROCESS OIL	17.00	8.47
ANTIOXIDANT TDQ	1.00	0.50
ANTIOXIDANT 6PPD	1.50	0.75
MC WAX/ WAX BLEND	2.00	1.00
STEARIC ACID	1.00	0.50
ZINC OXIDE	2.50	1.25
ACCELERATOR TBBS	1.50	0.75
SULFUR	1.80	0.90
ACCELERATOR DPG	1.50	0.75
TOTAL	200.65	100.00

Properties	Method	Typical Value
Tc90 @160°C (min)	ASTM D5289	8.6
Physical Properties (Cured @160°C/Tc90+2 Min)
300% Modulus (MPa)	ASTM D412	10.9
Tensile Strength (MPa)	ASTM D412	17.3
Elongation @ Break (%)	ASTM D412	407
Hardness (Shore A)	ASTM D2240	67
Abrasion Properties (Cured @160°C/Tc90+5 Min)
Abrasion Loss (mm³)	ASTM D5963	84
Rebound Resilience (Cured @160°C/Tc90+5 Min)
Rebound Resilience @25°C (%)	ISO 4662	50
Heat Build Up Properties (Cured @160°C/Tc90+5 Min) - 30Hz, 100°C, 7kg, 25 min
HBU (°C)	ASTM D623	16

TYRE TREAD -PASSENGER CAR RADIAL : PCRT 7

Ingredient	PHR	%
STYLAMER SBR-1723	82.50	38.20
CISAMER-1220	40.00	18.52
CARBON ISAF N220	70.00	32.41
PROCESS OIL	12.00	5.56
MC WAX/WAX BLEND	2.00	0.93
ANTIOXIDANT TQ	1.00	0.46
ANTIOXIDANT 6PPD	1.50	0.69
STEARIC ACID	1.00	0.46
ZINC OXIDE	2.50	1.16
ACCELERATOR TBBS	1.25	0.58
ACCELERATOR DPG	0.20	0.09
SOLUBLE SULFUR	2.00	0.93
TOTAL	215.95	100.00

Properties	Method	Typical Value
Tc90 @160°C (min)	ASTM D5289	9.1
Physical Properties (Cured @160°C/Tc90+2 Min)
300% Modulus (MPa)	ASTM D412	7.9
Tensile Strength (MPa)	ASTM D412	20.9
Elongation @ Break (%)	ASTM D412	567
Hardness (Shore A)	ASTM D2240	57
Abrasion Properties (Cured @160°C/Tc90+5 Min)
Abrasion Loss(mm³)	ASTM D5963	88
Rebound Resilience (Cured @160°C/Tc90+5 Min)
Rebound % @25°C	ISO 4662	43
Heat Build Up Properties (Cured @160°C/Tc90+5 Min) - 30Hz, 50°C, 7kg, 25 min
HBU (°C)	ASTM D623	28

TYRE TREAD -PASSENGER CAR (HIGH TRACTION) : PCRT 8

Ingredient	PHR	%
STYLAMER SBR-1739	82.50	38.20
CISAMER-1220	40.00	18.52
CARBON ISAF N220	70.00	32.41
PROCESS OIL	12.00	5.56
MC WAX/WAX BLEND	2.00	0.93
ANTIOXIDANT TQ	1.00	0.46
ANTIOXIDANT 6PPD	1.50	0.69
STEARIC ACID	1.00	0.46
ZINC OXIDE	2.50	1.16
ACCELERATOR TBBS	1.25	0.58
ACCELERATOR DPG	0.20	0.09
SOLUBLE SULFUR	2.00	0.93
TOTAL	215.95	100.00

Properties	Method	Typical Value
Tc90 @160°C (min)	ASTM D5289	9.7
Physical Properties (Cured @160°C/Tc90+2 Min)
300% Modulus (MPa)	ASTM D412	7.9
Tensile Strength (MPa)	ASTM D412	21.6
Elongation @ Break (%)	ASTM D412	597
Hardness (Shore A)	ASTM D2240	57
Abrasion Properties (Cured @160°C/Tc90+5 Min)
Abrasion Loss(mm³)	ASTM D5963	101
Rebound Resilience (Cured @160°C/Tc90+5 Min)
Rebound % @25°C	ISO 4662	34
Heat Build Up Properties (Cured @160°C/Tc90+5 Min) - 30Hz, 50°C, 7kg, 25 min
HBU (°C)	ASTM D623	27
Dynamic Properties (Cured @160°C/Tc90+2 Min)- 2% static strain,1% dynamic strain,10Hz-Tension mode
Tan δ @0°C	ASTM D5992	0.41
Tan δ @30°C	ASTM D5992	0.36

TYRE TREAD - TRUCK & BUS RIB : TBTR 1

Ingredient	PHR	%
NATURAL RUBBER (RSS 4)	50.00	28.90
CISAMER-01	50.00	28.90
CARBON HAF N330	50.00	28.90
AROMATIC OIL	8.00	4.62
ANTIOXIDANT TDQ	1.50	0.87
ANTIOXIDANT 6PPD	2.50	1.45
STEARIC ACID	2.00	1.16
ZINC OXIDE	4.00	2.31
CI RESIN	2.00	1.16
ACCELERATOR CBS	1.00	0.58
SULFUR	2.00	1.16
TOTAL	173.00	100.00

Properties	Method	Typical Value
Tc90 @145°C (min)	ASTM D2084	18.1
Physical Properties (Cured @145°C/Tc90+2 Min)
300% Modulus (MPa)	ASTM D412	8.7
Tensile Strength (MPa)	ASTM D412	21.6
Elongation @ Break (%)	ASTM D412	590
Hardness (Shore A)	ASTM D2240	62
Abrasion Properties (Cured @145°C/Tc90+5 Min)
Abrasion Loss (mm³)	ASTM D5963	67
Rebound Resilience (Cured @145°C/Tc90+5 Min)
Rebound Resilience @25°C (%)	ISO 4662	53
Heat Build Up Properties (Cured @145°C/Tc90+5 Min) - 30Hz, 100°C, 7 kg, 15 min
HBU (°C)	ASTM D623	19

TYRE TREAD - TRUCK & BUS RIB : TBTR 2

Ingredient	PHR	%
NATURAL RUBBER (RSS 4)	50.00	28.90
CISAMER-1220	50.00	28.90
CARBON HAF N330	50.00	28.90
AROMATIC OIL	8.00	4.62
ANTIOXIDANT TDQ	1.50	0.87
ANTIOXIDANT 6PPD	2.50	1.45
STEARIC ACID	2.00	1.16
ZINC OXIDE	4.00	2.31
CI RESIN	2.00	1.16
ACCELERATOR CBS	1.00	0.58
SULFUR	2.00	1.16
TOTAL	173.00	100.00

Properties	Method	Typical Value
Tc90 @145°C (min)	ASTM D2084	18.8
Physical Properties (Cured @145°C/Tc90+2 Min)
300% Modulus (MPa)	ASTM D412	9.5
Tensile Strength (MPa)	ASTM D412	20.7
Elongation @ Break (%)	ASTM D412	551
Hardness (Shore A)	ASTM D2240	63
Abrasion Properties (Cured @145°C/Tc90+5 Min)
Abrasion Loss (mm³)	ASTM D5963	69
Rebound Resilience (Cured @145°C/Tc90+5 Min)
Rebound Resilience @25°C (%)	ISO 4662	54
Heat Build Up Properties (Cured @145°C/Tc90+5 Min) - 30Hz, 100°C, 7kg, 25 min
HBU (°C)	ASTM D623	18

TYRE TREAD - TRUCK & BUS RIB : TBTR 3

Ingredient	PHR	%
NATURAL RUBBER (RSS 4)	50.00	28.90
CISAMER-700	50.00	28.90
CARBON HAF N330	50.00	28.90
PROCESS OIL	8.00	4.62
ANTIOXIDANT TDQ	1.50	0.87
ANTIOXIDANT 6PPD	2.50	1.45
STEARIC ACID	2.00	1.16
ZINC OXIDE	4.00	2.31
CI RESIN	2.00	1.16
ACCELERATOR CBS	1.00	0.58
SULFUR	2.00	1.16
TOTAL	173.00	100.00

Properties	Method	Typical Value
Tc90 @145°C (min)	ASTM D2084	18.1
Physical Properties (Cured @145°C/Tc90+2 Min)
300% Modulus (MPa)	ASTM D412	9.7
Tensile Strength (MPa)	ASTM D412	21
Elongation @ Break (%)	ASTM D412	556
Hardness (Shore A)	ASTM D2240	64
Abrasion Properties (Cured @145°C/Tc90+5 Min)
Abrasion Loss (mm³)	ASTM D5963	65
Rebound Resilience (Cured @145°C/Tc90+5 Min)
Rebound Resilience @25°C (%)	ISO 4662	56
Heat Build Up Properties (Cured @145°C/Tc90+5 Min) - 30Hz, 100°C, 7kg, 25 min
HBU (°C)	ASTM D623	16

TYRE TREAD - TRUCK & BUS RADIAL : TBRT 1

Ingredient	PHR	%
NATURAL RUBBER (RSS 4)	70.00	42.31
STYLAMER SBR-1502	30.00	18.13
CARBON ISAF-HS N234	55.00	33.23
ZINC OXIDE	4.00	2.42
STEARIC ACID	2.00	1.21
MC WAX/WAX BLEND	1.00	0.60
ANTIOXIDANT 6PPD	1.00	0.60
RETARDER PVI	0.20	0.12
ACCELERATOR CBS	1.00	0.60
ACCELERATOR DPG	0.30	0.18
SULFUR	1.00	0.60
TOTAL	165.50	100.00

Properties	Method	Typical Value
Tc90 @160°C (min)	ASTM D5289	5.7
Physical Properties (Cured @160°C/Tc90+2 Min)
300% Modulus (MPa)	ASTM D412	12.2
Tensile Strength (MPa)	ASTM D412	25.0
Elongation @ Break (%)	ASTM D412	546
Hardness (Shore A)	ASTM D2240	66
Abrasion Properties (Cured @160°C/Tc90+5 Min)
Abrasion Loss (mm^³)	ASTM D5963	112
Rebound Resilience (Cured @160°C/Tc90+5 Min)
Rebound Resilience @25°C(%)	ISO 4662	40

TYRE TREAD - OFF THE ROAD : OTRT 1

Ingredient	PHR	%
NATURAL RUBBER (RSS 4)	80.00	42.25
STYLAMER SBR-1502	20.00	10.56
CARBON HAF N330	49.00	25.88
PPT SILICA VN3	15.00	7.92
SILANE COUPLING AGENT X50S	2.40	1.27
HOMOGENISER	2.00	1.06
AROMATIC OIL	5.00	2.64
MC WAX/WAX BLEND	2.00	1.06
ANTIOXIDANT 6PPD	2.00	1.06
ANTIOXIDANT TQ	1.00	0.53
STEARIC ACID	2.00	1.06
ZINC OXIDE	4.00	2.11
PF RESIN	2.00	1.06
RETARDER CTP	0.20	0.11
ACCELERATOR TBBS	1.00	0.53
ACCELERATOR TMT	0.05	0.03
SOLUBLE SULFUR	1.70	0.90
TOTAL	189.35	100.00

Properties	Method	Typical Value
Tc90 @141°C (min)	ASTM D5289	25.7
Physical Properties (Cured @141°C/Tc90+2 Min)
300% Modulus (MPa)	ASTM D412	11.4
Tensile Strength (MPa)	ASTM D412	23.6
Elongation @ Break (%)	ASTM D412	572
Hardness (Shore A)	ASTM D2240	65
Tear Strength (N/mm)	ASTM D624	121
Abrasion Properties (Cured @141°C/Tc90+5 Min)
Abrasion Resistance Index(ARI)	ASTM D5963	137
Rebound Resilience (Cured @141°C/Tc90+5 Min)
Rebound % @25°C	ISO 4662	43
Rebound % @70°C	ISO 4662	60
Heat Build Up Properties (Cured @141°C/Tc90+5 Min) - 30Hz, 50°C, 7kg, 25 min
HBU (°C)	ASTM D623	29
Cut & Chip Resistance (Cured @141°C/Tc90+5 Min)
Weight Loss (grams)	EDM*	2.0

EDM*- ECSC Developed Method

TYRE TREAD - OFF THE ROAD : OTRT 2

Ingredient	PHR	%
NATURAL RUBBER (RSS 4)	60.00	31.98
STYLAMER SBR-1502	40.00	21.32
CARBON HAF-HS N339	45.00	23.99
PPT SILICA VN3	15.00	8.00
SILANE COUPLING AGENT X50S	2.40	1.28
HOMOGENISER	2.00	1.07
AROMATIC OIL	7.00	3.73
MC WAX/WAX BLEND	2.00	1.07
ANTIOXIDANT 6PPD	2.00	1.07
ANTIOXIDANT TQ	1.00	0.53
STEARIC ACID	2.00	1.07
ZINC OXIDE	4.00	2.13
PF RESIN	2.00	1.07
RETARDER CTP	0.30	0.16
ACCELERATOR TBBS	1.20	0.64
ACCELERATOR TMT	0.10	0.05
SOLUBLE SULFUR	1.60	0.85
TOTAL	187.60	100.00

Properties	Method	Typical Value
Tc90 @141°C (min)	ASTM D5289	27.8
Physical Properties (Cured @141°C/Tc90+2 Min)
300% Modulus (MPa)	ASTM D412	12.7
Tensile Strength (MPa)	ASTM D412	23.0
Elongation @ Break (%)	ASTM D412	550
Hardness (Shore A)	ASTM D2240	66
Tear Strength (N/mm)	ASTM D624	116
Abrasion Properties (Cured @141°C/Tc90+5 Min)
Abrasion Resistance Index(ARI)	ASTM D5963	132
Rebound Resilience (Cured @141°C/Tc90+5 Min)
Rebound % @25°C	ISO 4662	42
Rebound % @70°C	ISO 4662	58
Heat Build Up Properties (Cured @141°C/Tc90+5 Min) - 30Hz, 50°C, 7kg, 25 min
HBU (°C)	ASTM D623	31
Cut & Chip Resistance (Cured @141°C/Tc90+5 Min)
Weight Loss (grams)	EDM*	2.1

EDM*- ECSC Developed Method

TYRE TREAD - LIGHT COMMERCIAL : LCVT 1

Ingredient	PHR	%
NATURAL RUBBER (RSS 4)	30.00	16.18
PEPTISER	0.10	0.05
STYLAMER SBR-1502	30.00	16.18
CISAMER-01	40.00	21.57
CARBON HAF-HS N339	58.00	31.28
AROMATIC OIL	13.00	7.01
HOMOGENISER	1.50	0.81
ANTIOXIDANT TQ	1.00	0.54
ANTIOXIDANT 6PPD	1.50	0.81
STEARIC ACID	2.00	1.08
ZINC OXIDE	3.50	1.89
SP RESIN	2.00	1.08
RETARDER CTP	0.15	0.08
ACCELERATOR TBBS	0.80	0.43
SOLUBLE SULFUR	1.90	1.02
TOTAL	185.45	100.00

Properties	Method	Typical Value
Tc90 @150°C (min)	ASTM D5289	17.4
Physical Properties (Cured @150°C/Tc90+2 Min)
300% Modulus (MPa)	ASTM D412	7.9
Tensile Strength (MPa)	ASTM D412	19.6
Elongation @ Break (%)	ASTM D412	615
Hardness (Shore A)	ASTM D2240	62
Abrasion Properties (Cured @150°C/Tc90+5 Min)
Abrasion Loss (mm³)	ASTM D5963	64

TYRE SIDEWALL - TRUCK & BUS : TBSW 1

Ingredient	PHR	%
NATURAL RUBBER (RSS 4)	50.00	28.57
CISAMER-01	50.00	28.57
CARBON HAF N330	50.00	28.57
AROMATIC OIL	10.00	5.71
ANTIOXIDANT TDQ	1.00	0.57
ANTIOXIDANT 6PPD	2.00	1.14
MC WAX/ WAX BLEND	2.00	1.14
STEARIC ACID	2.00	1.14
ZINC OXIDE	3.00	1.71
CI RESIN	2.00	1.14
ACCELERATOR TBBS	0.90	0.51
SULFUR	2.00	1.14
RETARDER CTP	0.10	0.06
TOTAL	175.00	100.00

Properties	Method	Typical Value
Tc90 @145°C (min)	ASTM D5289	21.7
Physical Properties (Cured @145°C/Tc90+2 Min)
300% Modulus (MPa)	ASTM D412	7.8
Tensile Strength (MPa)	ASTM D412	21
Elongation @ Break (%)	ASTM D412	630
Hardness (Shore A)	ASTM D2240	58
Fatigue To Failure Testing (Cured @145°C/Tc90+2 Min)
Fatigue life (kC)	ASTM D4482	>200
Ozone Resistance (Cured @145°C/Tc90+2 Min)-72 hrs,25% Elongation ,40°C,50 pphm
Static Ozone	ASTM D1149	No Cracks Upto 72 hrs

TYRE SIDEWALL - TRUCK & BUS : TBSW 2

Ingredient	PHR	%
NATURAL RUBBER (RSS 4)	50.00	28.57
CISAMER-1220	50.00	28.57
CARBON HAF N330	50.00	28.57
AROMATIC OIL	10.00	5.71
ANTIOXIDANT TDQ	1.00	0.57
ANTIOXIDANT 6PPD	2.00	1.14
MC WAX/ WAX BLEND	2.00	1.14
STEARIC ACID	2.00	1.14
ZINC OXIDE	3.00	1.71
CI RESIN	2.00	1.14
ACCELERATOR TBBS	0.90	0.51
SULFUR	2.00	1.14
RETARDER CTP	0.10	0.06
TOTAL	175.00	100.00

Properties	Method	Typical Value
Tc90 @145°C (min)	ASTM D5289	21.9
Physical Properties (Cured @145°C/Tc90+2 Min)
300% Modulus (MPa)	ASTM D412	7.8
Tensile Strength (MPa)	ASTM D412	20
Elongation @ Break (%)	ASTM D412	603
Hardness (Shore A)	ASTM D2240	57
Fatigue To Failure Testing (Cured @145°C/Tc90+2 Min)
Fatigue life (kC)	ASTM D4482	>200
Ozone Resistance (Cured @145°C/Tc90+2 Min)-72 hrs,25% Elongation ,40°C,50 pphm
Static Ozone	ASTM D1149	No Cracks Upto 72 hrs

TYRE SIDEWALL - TRUCK & BUS : TBSW 3

Ingredient	PHR	%
NATURAL RUBBER (RSS 4)	50.00	28.57
CISAMER-700	50.00	28.57
CARBON HAF N330	50.00	28.57
PROCESS OIL	10.00	5.71
ANTIOXIDANT TDQ	1.00	0.57
ANTIOXIDANT 6PPD	2.00	1.14
MC WAX/ WAX BLEND	2.00	1.14
STEARIC ACID	2.00	1.14
ZINC OXIDE	3.00	1.71
CI RESIN	2.00	1.14
ACCELERATOR TBBS	0.90	0.51
SULFUR	2.00	1.14
RETARDER CTP	0.10	0.06
TOTAL	175.00	100.00

Properties	Method	Typical Value
Tc90 @145°C (min)	ASTM D5289	21.3
Physical Properties (Cured @145°C/Tc90+2 Min)
300% Modulus (MPa)	ASTM D412	8.0
Tensile Strength (MPa)	ASTM D412	21.0
Elongation @ Break (%)	ASTM D412	557
Hardness (Shore A)	ASTM D2240	59
Fatigue To Failure Testing (Cured @145°C/Tc90+2 Min)
Fatigue life (kC)	ASTM D4482	>200
Ozone Resistance (Cured @145°C/Tc90+2 Min)-72 hrs,25% Elongation ,40°C,50 pphm
Static Ozone	ASTM D1149	No Cracks Upto 72 hrs

TYRE SIDEWALL - TRUCK & BUS RADIAL : TBSW 4

Ingredient	PHR	%
NATURAL RUBBER (RSS 4)	30.00	18.27
CISAMER-01	50.00	30.45
STYLAMER SBR-1502	20.00	12.18
CARBON HAF-HS N339	45.00	27.41
AROMATIC OIL	4.00	2.44
PF RESIN	2.00	1.22
MC WAX/WAX BLEND	2.00	1.22
ANTIOXIDANT TMQ	1.00	0.61
ANTIOXIDANT 6PPD	3.00	1.83
ZINC OXIDE	4.00	2.44
STEARIC ACID	2.00	1.22
RETARDER PVI	0.20	0.12
ACCELERATOR CBS	1.00	0.61
SULFUR	1.20	0.73
TOTAL	164.20	100.00

Properties	Method	Typical Value
Tc90 @160°C (min)	ASTM D5289	8.4
Physical Properties (Cured @160°C/Tc90+2 Min)
300% Modulus (MPa)	ASTM D412	7.8
Tensile Strength (MPa)	ASTM D412	21.0
Elongation @ Break (%)	ASTM D412	630
Hardness (Shore A)	ASTM D2240	58
Fatigue To Failure Testing (Cured @160°C/Tc90+2 Min)
Fatigue life (kC)	ASTM D4482	>200
Ozone Resistance (Cured @160°C/Tc90+2 Min)-72 hrs,25% Elongation ,40°C,50 pphm
Static Ozone	ASTM D1149	No Cracks Upto 72 hrs

Tyre Ply - Truck & Bus Bias

Ingredient	PHR	%
NATURAL RUBBER (RSS 4)	50.00	27.15
STYLAMER SBR-1712	68.75	37.33
CARBON GPF N660	45.00	24.44
AROMATIC OIL	10.00	5.43
ANTIOXIDANT TQ	1.00	0.54
PF RESIN	2.00	1.09
ZINC OXIDE	3.00	1.63
STEARIC ACID	0.50	0.27
ACCELERATOR MBTS	0.80	0.43
ACCELERATOR DPG	0.10	0.05
INSOLUBLE SULFUR (OT20)	3.00	1.63
TOTAL	184.15	100.00

Properties	Method	Typical Value
Tc90 @160°C (min)	ASTM D5289	7.0
Physical Properties (Cured @160°C/Tc90+2 Min)
300% Modulus (MPa)	ASTM D412	13.9
Tensile Strength (MPa)	ASTM D412	14.8
Elongation @ Break (%)	ASTM D412	317
Hardness (Shore A)	ASTM D2240	62
Tack Properties (Constant force 500 gmf/30 min, Width 12.5 mm)
Seperation force (gmf)	*EDM	1700
H-adhesion :1680/2D Nylon 6 cord (Cured @160°C/Tc90+2 min)
Seperation force (Kgf)	ASTM D4776	14
Heat Build Up Properties (Cured @160°C/Tc90+5 min)- 30 Hz, 100°C, 7 kg, 25 min
HBU (°C)	ASTM D623	11

*EDM - ECSC Developed Method

Tyre Bead - Truck & Bus Bias

Ingredient	PHR	%
STYLAMER SBR-1502	100.00	37.68
CARBON GPF N660	110.00	41.45
AROMATIC OIL	18.00	6.78
PF RESIN	2.00	0.75
STEARIC ACID	2.50	0.94
ZINC OXIDE	5.00	1.88
PPT SILICA VN3	14.50	5.46
PF RESIN	2.00	0.75
ANTIOXIDANT 6PPD	1.00	0.38
RESORCINOL	2.50	0.94
ACCELERATOR CBS	1.20	0.45
HMMM (65%)	0.20	0.08
SULFUR	2.00	0.75
ZINC OXIDE	2.00	0.75
INSOLUBLE SULFUR (OT20)	2.50	0.94
TOTAL	265.40	100.00

Properties	Method	Typical Value
Tc90 @150°C (min)	ASTM D5289	34.6
Physical Properties (Cured @150°C/Tc90+2 Min)
100% Modulus (MPa)	ASTM D412	8.1
Tensile Strength (MPa)	ASTM D412	14.6
Elongation @ Break (%)	ASTM D412	228
Hardness (Shore A)	ASTM D2240	83
Bead-Wire Adhesion (Cured @150°C/Tc90+5 min, Wire size 0.965 mm)
Average Adhesion (N)	ASTM D1871	1010
Rebound Resilience (Cured @150°C/Tc90+5 Min)
Rebound Resilience @25°C (%)	ISO 4662	32
Rebound Resilience @70°C (%)	ISO 4662	41

TYRE BEAD - TRUCK & BUS RADIAL

Ingredient	PHR	%
STYLAMER SBR-1502	50.00	19.36
STYLAMER SBR-1712	68.75	26.63
CARBON HAF N330	60.00	23.24
CARBON FEF N550	50.00	19.36
AROMATIC OIL	10.00	3.87
PF RESIN (TACKIFIER)	4.00	1.55
PF RESIN (HARDNER)	5.00	1.94
ANTIOXIDANT 6PPD	1.00	0.39
STEARIC ACID	1.00	0.39
ZINC OXIDE	3.50	1.36
RETARDER PVI	0.20	0.08
ACCELERATOR MBS	1.00	0.39
INSOLUBLE SULFUR (OT20)	3.75	1.45
TOTAL	258.20	100.00

Properties	Method	Typical Value
Tc90 @160°C (min)	ASTM D5289	14.1
Physical Properties (Cured @160°C/Tc90+2 Min)
300% Modulus (MPa)	ASTM D412	NIL
Tensile Strength (MPa)	ASTM D412	17.2
Elongation @ Break (%)	ASTM D412	257
Hardness (Shore A)	ASTM D2240	58
Bead-Wire Adhesion (Cured @160°C/Tc90+5 min, Wire size 0.965 mm)
Average Adhesion (N)	ASTM D1871	852
Rebound Resilience (Cured @160°C/Tc90+5 Min)
Rebound Resilience @25°C(%)	ISO 4662	29

Tyre tread- Motorcycle : MCT 1

Ingredient	PHR	%
STYLAMER SBR-1502	70.00	38.91
CISAMER-700	30.00	16.68
CRUMB RUBBER (40 MESH)	10.00	5.56
CARBON HAF N330	50.00	27.79
PROCESS OIL	8.00	4.45
ANTIOXIDANT TQ	1.00	0.56
ANTIOXIDANT 6PPD	1.00	0.56
MC WAX/WAX BLEND	1.00	0.56
STEARIC ACID	2.00	1.11
ZINC OXIDE	4.00	2.22
ACCELERATOR CBS	1.00	0.56
SULFUR	1.90	1.06
TOTAL	179.90	100.00

Properties	Method	Typical Value
Tc90 @160°C (min)	ASTM D5289	9.2
Physical Properties (Cured @160°C/Tc90+2 min)
300% Modulus (MPa)	ASTM D412	9.1
Tensile Strength (MPa)	ASTM D412	14.7
Elongation @ Break (%)	ASTM D412	445
Hardness (Shore A)	ASTM D2240	61
Heat Build Up Properties (Cured @160°C/Tc90+5 min)- 30 Hz, 50°C, 7 kg, 25 min
HBU (°C)	ASTM D623	28
Abrasion Properties (Cured @160°C/ Tc90+5 min)
Abrasion Loss (mm³)	ASTM D5963	86
Dynamic Properties (Cured @160°C/ Tc90+2 min)- 2% static strain, 1% dynamic strain, 1 Hz- Tension mode
Tan δ @30°C	ASTM D5992	0.23
Tan δ @70°C	ASTM D5992	0.19

Tyre tread- Motorcycle : MCT 2

Ingredient	PHR	%
STYLAMER SBR-1502	70.00	38.23
CISAMER-700	30.00	16.38
CRUMB RUBBER (40 MESH)	10.00	5.46
CARBON HAF N330	45.00	24.58
PPT SILICA VN3	8.00	4.37
PROCESS OIL	8.00	4.37
ANTIOXIDANT TQ	1.00	0.55
ANTIOXIDANT 6PPD	1.00	0.55
MC WAX/WAX BLEND	1.00	0.55
STEARIC ACID	2.00	1.09
ZINC OXIDE	4.00	2.18
ACCELERATOR CBS	1.20	0.66
SULFUR	1.90	1.04
TOTAL	183.10	100.00

Properties	Method	Typical Value
Tc90 @160°C (min)	ASTM D5289	9.3
Physical Properties (Cured @160°C/Tc90+2 min)
300% Modulus (MPa)	ASTM D412	8.2
Tensile Strength (MPa)	ASTM D412	14.2
Elongation @ Break (%)	ASTM D412	472
Hardness (Shore A)	ASTM D2240	61
Heat Build Up Properties (Cured @160°C/Tc90+5 min)- 30 Hz, 50°C, 7 kg, 25 min
HBU (°C)	ASTM D623	28
Abrasion Properties (Cured @160°C/ Tc90+5 min)
Abrasion Loss (mm³)	ASTM D5963	88
Dynamic Properties (Cured @160°C/ Tc90+2 min)- 2% static strain, 1% dynamic strain, 1 Hz- Tension mode
Tan δ @30°C	ASTM D5992	0.23
Tan δ @70°C	ASTM D5992	0.19

Tyre tread- Motorcycle : MCT 3

Ingredient	PHR	%
STYLAMER SBR-1502	70.00	35.33
STYLAMER SBR-1712	41.25	20.82
CRUMB RUBBER (40 MESH)	10.00	5.05
CARBON HAF N330	60.00	30.28
AROMATIC OIL	5.00	2.52
ANTIOXIDANT TQ	1.00	0.50
ANTIOXIDANT 6PPD	1.00	0.50
MC WAX/WAX BLEND	1.00	0.50
STEARIC ACID	2.00	1.01
ZINC OXIDE	4.00	2.02
ACCELERATOR CBS	1.20	0.61
SULFUR	1.70	0.86
TOTAL	198.15	100.00

Properties	Method	Typical Value
Tc90 @160°C (min)	ASTM D5289	9.4
Physical Properties (Cured @ 160 °C/ Tc90+2 min)
300% Modulus (MPa)	ASTM D412	9.3
Tensile Strength (MPa)	ASTM D412	16.5
Elongation @ Break (%)	ASTM D412	484
Hardness (Shore A)	ASTM D2240	61
Heat Build Up Properties (Cured @160°C/ Tc90+5 min)- 30 Hz, 50°C, 7 kg, 25 min
HBU (°C)	ASTM D623	29
Abrasion Properties (Cured @160°C/ Tc90+5 min)
Abrasion Loss (mm³)	ASTM D5963	97
Dynamic Properties (Cured @160°C/ Tc90+2 min)- 2% static strain, 1% dynamic strain, 1 Hz- Tension mode
Tan δ @30°C	ASTM D5992	0.28
Tan δ @70°C	ASTM D5992	0.24

TYRE TREAD- MOTORCYCLE : MCT 4

Ingredient	PHR	%
STYLAMER SBR-1502	40.00	20.78
STYLAMER SBR-1712	41.25	21.43
CISAMER-01	30.00	15.59
CARBON HAF N330	65.00	33.78
AROMATIC OIL	5.00	2.60
MC WAX/WAX BLEND	1.00	0.52
ANTIOXIDANT TQ	1.00	0.52
ANTIOXIDANT 6PPD	1.00	0.52
STEARIC ACID	2.00	1.04
ZINC OXIDE	4.00	2.08
ACCELERATOR CBS	1.20	0.10
SOLUBLE SULFUR	2.00	1.04
TOTAL	192.45	100.00

Properties	Method	Typical Value
Tc90 @160°C (min)	ASTM D5289	9.5
Physical Properties (Cured @160°C/Tc90+2 Min)
300% Modulus (MPa)	ASTM D412	11.3
Tensile Strength (MPa)	ASTM D412	21.8
Elongation @ Break (%)	ASTM D412	497
Hardness (Shore A)	ASTM D2240	62
Abrasion Properties (Cured @160°C/ Tc90+5 min)
Abrasion Loss (mm³)	ASTM D5963	75
Dynamic Properties (Cured @160°C/Tc90+2 Min)- 2% static strain, 1% dynamic strain, 10Hz - Tension mode
Tan δ @30°C	ASTM D5992	0.28
Tan δ @60°C	ASTM D5992	0.24

TYRE TREAD- MOTORCYCLE : MCT 5

Ingredient	PHR	%
STYLAMER SBR-1502	40.00	20.78
STYLAMER SBR-1712	41.25	21.43
CISAMER-1220	30.00	15.59
CARBON HAF N330	65.00	33.78
AROMATIC OIL	5.00	2.60
MC WAX/WAX BLEND	1.00	0.52
ANTIOXIDANT TQ	1.00	0.52
ANTIOXIDANT 6PPD	1.00	0.52
STEARIC ACID	2.00	1.04
ZINC OXIDE	4.00	2.08
ACCELERATOR CBS	1.20	0.10
SOLUBLE SULFUR	2.00	1.04
TOTAL	192.45	100.00

Properties	Method	Typical Value
Tc90 @160°C (min)	ASTM D5289	9.1
Physical Properties (Cured @160°C/Tc90+2 Min)
300% Modulus (MPa)	ASTM D412	11.6
Tensile Strength (MPa)	ASTM D412	22.3
Elongation @ Break (%)	ASTM D412	509
Hardness (Shore A)	ASTM D2240	63
Abrasion Properties (Cured @160°C/ Tc90+5 min)
Abrasion Loss (mm³)	ASTM D5963	71
Dynamic Properties (Cured @160°C/Tc90+2 Min)- 2% static strain, 1% dynamic strain, 10Hz - Tension mode
Tan δ @30°C	ASTM D5992	0.28
Tan δ @60°C	ASTM D5992	0.24

TYRE TREAD- MOTORCYCLE (HIGH MILEAGE) : MCT 6

Ingredient	PHR	%
STYLAMER SBR-1502	40.00	20.78
STYLAMER SBR-1723	41.25	21.43
CISAMER-1220	30.00	15.59
CARBON HAF N330	65.00	33.78
PROCESS OIL	5.00	2.60
MC WAX/WAX BLEND	1.00	0.52
ANTIOXIDANT TQ	1.00	0.52
ANTIOXIDANT 6PPD	1.00	0.52
STEARIC ACID	2.00	1.04
ZINC OXIDE	4.00	2.08
ACCELERATOR CBS	1.20	0.10
SOLUBLE SULFUR	2.00	1.04
TOTAL	192.45	100.00

Properties	Method	Typical Value
Tc90 @160°C (min)	ASTM D5289	9.3
Physical Properties (Cured @160°C/Tc90+2 Min)
300% Modulus (MPa)	ASTM D412	11.6
Tensile Strength (MPa)	ASTM D412	22.2
Elongation @ Break (%)	ASTM D412	505
Hardness (Shore A)	ASTM D2240	63
Abrasion Properties (Cured @160°C/ Tc90+5 min)
Abrasion Loss (mm³)	ASTM D5963	67
Dynamic Properties (Cured @160°C/Tc90+2 Min)- 2% static strain, 1% dynamic strain, 10Hz - Tension mode
Tan δ @30°C	ASTM D5992	0.26
Tan δ @60°C	ASTM D5992	0.22

TYRE TREAD - MOTORCYCLE (HIGH TRACTION) : MCT 7

Ingredient	PHR	%
STYLAMER SBR-1502	40.00	20.78
STYLAMER SBR-1739	41.25	21.43
CISAMER-1220	30.00	15.59
CARBON HAF N330	65.00	33.78
PROCESS OIL	5.00	2.60
MC WAX/WAX BLEND	1.00	0.52
ANTIOXIDANT TQ	1.00	0.52
ANTIOXIDANT 6PPD	1.00	0.52
STEARIC ACID	2.00	1.04
ZINC OXIDE	4.00	2.08
ACCELERATOR CBS	1.20	0.10
SOLUBLE SULFUR	2.00	1.04
TOTAL	192.45	100.00

Properties	Method	Typical Value
Tc90 @160°C (min)	ASTM D5289	9.7
Physical Properties (Cured @160°C/Tc90+2 Min)
300% Modulus (MPa)	ASTM D412	11.3
Tensile Strength (MPa)	ASTM D412	22.2
Elongation @ Break (%)	ASTM D412	514
Hardness (Shore A)	ASTM D2240	63
Abrasion Properties (Cured @160°C/ Tc90+5 min)
Abrasion Loss (mm³)	ASTM D5963	73.00
Dynamic Properties (Cured @160°C/Tc90+2 Min)- 2% static strain, 1% dynamic strain, 10Hz - Tension mode
Tan δ @30°C	ASTM D5992	0.29
Tan δ @60°C	ASTM D5992	0.23

TYRE TREAD - MOTORCYCLE (HIGH GRIP) : MCT 8

Ingredient	PHR	%
STYLAMER SBR-1739	82.50	39.78
CISAMER-01	40.00	19.29
CARBON HAF N330	70.00	33.75
PROCESS OIL	3.00	1.45
MC WAX/WAX BLEND	1.00	0.48
ANTIOXIDANT TQ	1.00	0.48
ANTIOXIDANT 6PPD	1.00	0.48
STEARIC ACID	2.00	0.96
ZINC OXIDE	4.00	1.93
ACCELERATOR CBS	1.20	0.58
SOLUBLE SULFUR	1.70	0.82
TOTAL	207.40	100.00

Properties	Method	Typical Value
Tc90 @160°C (min)	ASTM D5289	9.8
Physical Properties (Cured @160°C/Tc90+2 Min)
300% Modulus (MPa)	ASTM D412	11.3
Tensile Strength (MPa)	ASTM D412	20.4
Elongation @ Break (%)	ASTM D412	490
Hardness (Shore A)	ASTM D2240	62
Abrasion Properties (Cured @160°C/ Tc90+5 min)
Abrasion Loss (mm³)	ASTM D5963	85
Dynamic Properties (Cured @160°C/Tc90+2 Min)- 2% static strain, 1% dynamic strain, 10Hz - Tension mode
Tan δ @30°C	ASTM D5992	0.31
Tan δ @70°C	ASTM D5992	0.24

TYRE TREAD - MOTORCYCLE (HIGH GRIP-HIGH MILEAGE) : MCT 9

Ingredient	PHR	%
STYLAMER SBR-1739	68.75	33.43
CISAMER-01	50.00	24.31
CARBON HAF N330	70.00	34.04
PROCESS OIL	5.00	2.43
MC WAX/WAX BLEND	1.00	0.49
ANTIOXIDANT TQ	1.00	0.49
ANTIOXIDANT 6PPD	1.00	0.49
STEARIC ACID	2.00	0.97
ZINC OXIDE	4.00	1.95
ACCELERATOR CBS	1.20	0.58
SOLUBLE SULFUR	1.70	0.83
TOTAL	205.65	100.00

Properties	Method	Typical Value
Tc90 @160°C (min)	ASTM D5289	9.0
Physical Properties (Cured @160°C/Tc90+2 Min)
300% Modulus (MPa)	ASTM D412	11.3
Tensile Strength (MPa)	ASTM D412	20.7
Elongation @ Break (%)	ASTM D412	488
Hardness (Shore A)	ASTM D2240	62
Abrasion Properties (Cured @160°C/Tc90+5 Min)
Abrasion Loss (mm³)	ASTM D5963	60
Dynamic Properties (Cured @160°C/Tc90+2 Min)- 2% static strain, 1% dynamic strain, 10Hz - Tension mode
Tan δ @30°C	ASTM D5992	0.28
Tan δ @70°C	ASTM D5992	0.21

TYRE TREAD- SCOOTER - REGULAR : STT1

Ingredient	PHR	%
STYLAMER SBR-1502	22.00	9.54
STYLAMER SBR-1712	55.70	24.16
CISAMER-01	35.00	15.18
CRUMB RUBBER (80 MESH)	5.00	2.17
WHOLE TYRE RECLAIM	5.00	2.17
CARBON HAF-HS N375	75.00	32.53
HOMOGENISER	2.00	0.87
AROMATIC OIL	16.00	6.94
MC WAX/WAX BLEND	2.00	0.87
ANTIOXIDANT TQ	2.00	0.87
ANTIOXIDANT 6PPD	1.50	0.65
STEARIC ACID	1.50	0.65
ZINC OXIDE	3.00	1.30
PF RESIN	2.00	0.87
ACCELERATOR TBBS	1.20	0.52
ACCELERATOR DPG	0.15	0.07
SOLUBLE SULFUR	1.50	0.65
TOTAL	230.55	100.00

Properties	Method	Typical Value
Tc90 @160°C (min)	ASTM D5289	9.6
Physical Properties (Cured @160°C/Tc90+2 Min)
300% Modulus (MPa)	ASTM D412	6.9
Tensile Strength (MPa)	ASTM D412	16.7
Elongation @ Break (%)	ASTM D412	590
Hardness (Shore A)	ASTM D2240	59
Abrasion Properties (Cured @160°C/Tc90+5 Min)
Abrasion Loss (mm³)	ASTM D5963	75
Rebound Resilience (Cured @160°C/Tc90+5 Min)
Rebound % @25°C	ISO 4662	36
Rebound % @70°C	ISO 4662	43

TYRE TREAD- SCOOTER (LOW RR ) : STT 2

Ingredient	PHR	%
STYLAMER SBR-1502	22.00	9.54
STYLAMER SBR-1723	55.70	24.16
CISAMER-01	35.00	15.18
CRUMB RUBBER (80 MESH)	5.00	2.17
WHOLE TYRE RECLAIM	5.00	2.17
CARBON HAF-HS N375	75.00	32.53
HOMOGENISER	2.00	0.87
AROMATIC OIL	16.00	6.94
MC WAX/WAX BLEND	2.00	0.87
ANTIOXIDANT TQ	2.00	0.87
ANTIOXIDANT 6PPD	1.50	0.65
ZINC OXIDE	3.00	1.30
STEARIC ACID	1.50	0.65
PF RESIN	2.00	0.87
ACCELERATOR TBBS	1.20	0.52
ACCELERATOR DPG	0.15	0.07
SOLUBLE SULFUR	1.50	0.65
TOTAL	230.55	100.00

Properties	Method	Typical Value
Tc90 @160°C (min)	ASTM D5289	9.2
Physical Properties (Cured @160°C/Tc90+2 Min)
300% Modulus (MPa)	ASTM D412	6.9
Tensile Strength (MPa)	ASTM D412	16.8
Elongation @ Break (%)	ASTM D412	590
Hardness (Shore A)	ASTM D2240	58
Abrasion Properties (Cured @160°C/Tc90+5 Min)
Abrasion Loss (mm³)	ASTM D5963	73
Rebound Resilience (Cured @160°C/Tc90+5 Min)
Rebound % @25°C	ISO 4662	38
Rebound % @70°C	ISO 4662	46

TYRE TREAD - SCOOTER (HIGH TRACTION) : STT 3

Ingredient	PHR	%
STYLAMER SBR-1502	22.00	9.54
STYLAMER SBR-1739	55.70	24.16
CISAMER-01	35.00	15.18
CRUMB RUBBER (80 MESH)	5.00	2.17
WHOLE TYRE RECLAIM	5.00	2.17
CARBON HAF-HS N375	75.00	32.53
HOMOGENISER	2.00	0.87
AROMATIC OIL	16.00	6.94
MC WAX/WAX BLEND	2.00	0.87
ANTIOXIDANT TQ	2.00	0.87
ANTIOXIDANT 6PPD	1.50	0.65
ZINC OXIDE	3.00	1.30
STEARIC ACID	1.50	0.65
PF RESIN	2.00	0.87
ACCELERATOR TBBS	1.20	0.52
ACCELERATOR DPG	0.15	0.07
SOLUBLE SULFUR	1.50	0.65
TOTAL	230.55	100.00

Properties	Method	Typical Value
Tc90 @160°C (min)	ASTM D5289	9.7
Physical Properties (Cured @160°C/Tc90+2 Min)
300% Modulus (MPa)	ASTM D412	7.1
Tensile Strength (MPa)	ASTM D412	16.5
Elongation @ Break (%)	ASTM D412	598
Hardness (Shore A)	ASTM D2240	59
Abrasion Properties (Cured @160°C/Tc90+5 Min)
Abrasion Loss (mm³)	ASTM D5963	86
Rebound Resilience (Cured @160°C/Tc90+5 Min)
Rebound % @25°C	ISO 4662	32
Rebound % @70°C	ISO 4662	43

Cycle Tyre tread - Regular : CTT 1

Ingredient	PHR	%
NATURAL RUBBER (RSS 4)	20.00	7.99
STYLAMER SBR-1502	25.00	9.99
CISAMER-01	30.00	11.99
WHOLE TYRE RECLAIM	50.00	19.98
CRUMB RUBBER (40 MESH)	15.00	5.99
CARBON HAF N330	40.00	15.99
CHINA CLAY	40.00	15.99
AROMATIC OIL	15.00	5.99
PARAFFIN WAX	3.00	1.20
ANTIOXIDANT 6PPD	0.50	0.20
ANTIOXIDANT TDQ	1.50	0.60
STEARIC ACID	2.00	0.80
ZINC OXIDE	4.00	1.60
PF RESIN	1.00	0.40
ACCELERATOR CBS	1.10	0.44
ACCELERATOR TMT	0.12	0.05
SULFUR	2.00	0.80
TOTAL	250.22	100.00

Properties	Method	Typical Value
Tc90 @160°C (min)	ASTM D5289	5.6
Physical Properties (Cured @ 160°C/Tc90+2 min)
300% Modulus (MPa)	ASTM D412	6.7
Tensile Strength (MPa)	ASTM D412	8.9
Elongation @ Break (%)	ASTM D412	396
Hardness (Shore A)	ASTM D2240	67
Tension Set (%)	IS 3400	8.0
Percentage Retention - 70°C, 7 days
Tensile Strength (%)	ASTM D412	110
Elongation @ Break (%)	ASTM D412	79

Cycle Tyre tread - Regular : CTT 2

Ingredient	PHR	%
NATURAL RUBBER (RSS 4)	20.00	7.45
STYLAMER SBR-1502	25.00	9.32
CISAMER-01	30.00	11.18
WHOLE TYRE RECLAIM	50.00	18.63
CRUMB RUBBER (40 MESH)	20.00	7.45
CARBON HAF N330	40.00	14.91
CHINA CLAY	50.00	18.63
AROMATIC OIL	18.00	6.71
PARAFFIN WAX	3.00	1.12
ANTIOXIDANT 6PPD	0.50	0.19
ANTIOXIDANT TDQ	1.50	0.56
STEARIC ACID	2.00	0.75
ZINC OXIDE	4.00	1.49
PF RESIN	1.00	0.37
ACCELERATOR CBS	1.20	0.45
ACCELERATOR TMT	0.12	0.04
SULFUR	2.00	0.75
TOTAL	268.32	100.00

Properties	Method	Typical Value
Tc90 @160°C (min)	ASTM D5289	6.0
Physical Properties (Cured @ 160°C/Tc90+2 min)
300% Modulus (MPa)	ASTM D412	6.4
Tensile Strength (MPa)	ASTM D412	9.1
Elongation @ Break (%)	ASTM D412	428
Hardness (Shore A)	ASTM D2240	66
Tension Set (%)	IS 3400	7.2
Percentage Retention - 70°C, 7 days
Tensile Strength (%)	ASTM D412	104
Elongation @ Break (%)	ASTM D412	67

Cycle Tyre tread - Regular : CTT 3

Ingredient	PHR	%
NATURAL RUBBER (RSS 4)	20.00	7.02
STYLAMER SBR-1712	34.40	12.08
CISAMER-01	25.00	8.78
WHOLE TYRE RECLAIM	60.00	21.07
CRUMB RUBBER (40 MESH)	15.00	5.27
CARBON HAF N330	45.00	15.80
CHINA CLAY	50.00	17.55
AROMATIC OIL	20.00	7.02
PARAFFIN WAX	3.00	1.05
ANTIOXIDANT 6PPD	0.50	0.18
ANTIOXIDANT TDQ	1.50	0.53
STEARIC ACID	2.00	0.70
ZINC OXIDE	4.00	1.40
PF RESIN	1.00	0.35
ACCELERATOR CBS	1.30	0.46
ACCELERATOR TMT	0.12	0.04
SULFUR	2.00	0.70
TOTAL	284.82	100.00

Properties	Method	Typical Value
Tc90 @160°C (min)	ASTM D5289	6.5
Physical Properties (Cured @ 160°C/Tc90+2 min)
300% Modulus (MPa)	ASTM D412	6.7
Tensile Strength (MPa)	ASTM D412	8.8
Elongation @ Break (%)	ASTM D412	396
Hardness (Shore A)	ASTM D2240	67
Tension Set (%)	IS 3400	7.7
Percentage Retention - 70°C, 7 days
Tensile Strength (%)	ASTM D412	101
Elongation @ Break (%)	ASTM D412	72

Cycle Tyre tread - SBR rich : CTT 4

Ingredient	PHR	%
NATURAL RUBBER (RSS 4)	10.00	3.65
STYLAMER SBR-1502	50.00	18.23
CISAMER-01	15.00	5.47
WHOLE TYRE RECLAIM	50.00	18.23
CRUMB RUBBER (40 MESH)	15.00	5.47
CARBON HAF N330	40.00	14.58
CALCIUM CARBONATE	10.00	3.65
CHINA CLAY	55.00	20.05
AROMATIC OIL	16.00	5.83
PF RESIN	1.00	0.36
PARAFFIN WAX	2.00	0.73
ANTIOXIDANT TDQ	1.00	0.36
STEARIC ACID	2.00	0.73
ZINC OXIDE	4.00	1.46
ACCELERATOR CBS	1.80	0.66
ACCELERATOR TMT	0.20	0.07
SULFUR	1.30	0.47
TOTAL	274.30	100.00

Properties	Method	Typical Value
Tc90 @160°C (min)	ASTM D5289	3.8
Physical Properties (Cured @160°C/Tc90+2 min)
300% Modulus (MPa)	ASTM D412	6.4
Tensile Strength (MPa)	ASTM D412	8.7
Elongation @ Break (%)	ASTM D412	413
Hardness (Shore A)	ASTM D2240	68
Tension Set (%)	IS 3400	8.1
Percentage Retention - 70°C, 7 days
Tensile Strength (%)	ASTM D412	108
Elongation @ Break (%)	ASTM D412	78

Cycle Tyre tread - SBR rich : CTT 5

Ingredient	PHR	%
NATURAL RUBBER (RSS 4)	10.00	3.58
STYLAMER SBR-1502	60.00	21.48
CISAMER-01	10.00	3.58
WHOLE TYRE RECLAIM	40.00	14.32
CRUMB RUBBER (40 MESH)	15.00	5.37
CARBON HAF N330	50.00	17.90
CALCIUM CARBONATE	10.00	3.58
CHINA CLAY	55.00	19.69
AROMATIC OIL	16.00	5.73
PF RESIN	1.00	0.36
PARAFFIN WAX	2.00	0.72
ANTIOXIDANT TDQ	1.00	0.36
STEARIC ACID	2.00	0.72
ZINC OXIDE	4.00	1.43
ACCELERATOR CBS	1.80	0.64
ACCELERATOR TMT	0.20	0.07
SULFUR	1.30	0.47
TOTAL	279.30	100.00

Properties	Method	Typical Value
Tc90 @160°C (min)	ASTM D5289	4.0
Physical Properties (Cured @160°C/Tc90+2 min)
300% Modulus (MPa)	ASTM D412	6.8
Tensile Strength (MPa)	ASTM D412	9.1
Elongation @ Break (%)	ASTM D412	417
Hardness (Shore A)	ASTM D2240	69
Tension Set (%)	IS 3400	9.8
Percentage Retention - 70°C, 7 days
Tensile Strength (%)	ASTM D412	111
Elongation @ Break (%)	ASTM D412	76

Cycle Tyre tread - SBR rich : CTT 6

Ingredient	PHR	%
NATURAL RUBBER (RSS 4)	10.00	3.58
STYLAMER SBR-1502	70.00	25.06
WHOLE TYRE RECLAIM	40.00	14.32
CRUMB RUBBER (40 MESH)	15.00	5.37
CARBON HAF N330	50.00	17.90
CALCIUM CARBONATE	10.00	3.58
CHINA CLAY	55.00	19.69
AROMATIC OIL	16.00	5.73
PF RESIN	1.00	0.36
PARAFFIN WAX	2.00	0.72
ANTIOXIDANT TDQ	1.00	0.36
STEARIC ACID	2.00	0.72
ZINC OXIDE	4.00	1.43
ACCELERATOR CBS	1.80	0.64
ACCELERATOR TMT	0.20	0.07
SULFUR	1.30	0.47
TOTAL	279.30	100.00

Properties	Method	Typical Value
Tc90 @160°C (min)	ASTM D5289	3.9
Physical Properties (Cured @160°C/Tc90+2 min)
300% Modulus (MPa)	ASTM D412	7.0
Tensile Strength (MPa)	ASTM D412	9.8
Elongation @ Break (%)	ASTM D412	431
Hardness (Shore A)	ASTM D2240	68
Tension Set (%)	IS 3400	10.0
Percentage Retention - 70°C, 7 days
Tensile Strength (%)	ASTM D412	107
Elongation @ Break (%)	ASTM D412	80

CYCLE TYRE TREAD - OE SBR RICH : COTTON

Ingredient	PHR	%
NATURAL RUBBER (RSS 4)	30.00	10.39
STYLAMER SBR 1712	51.56	17.86
RECLAIM RUBBER	65.00	22.51
CARBON HAF N330	55.00	19.05
CHINA CLAY	55.00	19.05
AROMATIC OIL	17.00	5.89
MC WAX/WAX BLEND	3.00	1.04
ANTIOXIDANT TQ	1.00	0.35
ANTIOXIDANT 6PPD	0.50	0.17
STEARIC ACID	2.00	0.69
ZINC OXIDE	3.00	1.04
CP 90	2.00	0.69
ACCELERATOR CBS	1.30	0.45
ACCELERATOR TMTD	0.15	0.05
SOLUBLE SULFUR	2.20	0.76
TOTAL	288.71	100.00

Properties	Method	Typical Value
Tc90 @160°C (min)	ASTM D5289	3.7
Physical Properties (Cured @160°C/Tc90+2 min)
300% Modulus (kgf/cm²)	ASTM D412	90.0
Tensile Strength (kgf/cm²)	ASTM D412	113
Elongation @ Break (%)	ASTM D412	385
Hardness (Shore A)	ASTM D2240	66
Abrasion Properties (Cured @160°C/Tc90+5 Min)
Abrasion Resistance Index (ARI)	ASTM D5963	233

CYCLE TYRE TREAD - OE SBR RICH : NYLON

Ingredient	PHR	%
NATURAL RUBBER (RSS 4)	30.00	11.03
STYLAMER SBR 1712	48.13	17.70
CISAMER 01	10.00	3.68
RECLAIM RUBBER	50.00	18.39
CARBON HAF N330	60.00	22.06
CRUMB RUBBER	10.00	3.68
CHINA CLAY	30.00	11.03
AROMATIC OIL	18.00	6.62
MC WAX/WAX BLEND	2.00	0.74
ANTIOXIDANT TQ	1.50	0.55
ANTIOXIDANT 6PPD	0.50	0.18
STEARIC ACID	2.00	0.74
ZINC OXIDE	4.00	1.47
CP 90	2.00	0.74
ACCELERATOR CBS	1.40	0.51
ACCELERATOR TMTD	0.15	0.06
SOLUBLE SULFUR	2.25	0.83
TOTAL	271.93	100.00

Properties	Method	Typical Value
Tc90 @160°C (min)	ASTM D5289	4.2
Physical Properties (Cured @160°C/Tc90+2 min)
300% Modulus (kgf/cm2)	ASTM D412	91.5
Tensile Strength (kgf/cm2)	ASTM D412	124
Elongation @ Break (%)	ASTM D412	396
Hardness (Shore A)	ASTM D2240	64
Abrasion Properties (Cured @160°C/Tc90+5 Min)
Abrasion Resistance Index (ARI)	ASTM D5963	190

ACID TANK LINER

Ingredient	PHR	%
BROMOBUTYL IMPRAMER B2232	60.00	29.25
NR ( RSS4)	40.00	19.50
STEARIC ACID	1.00	0.49
CARBON GPF N660	25.00	12.19
CARBON HAF 330	25.00	12.19
BARYATES	25.00	12.19
NAPHTHENIC OIL	18.00	8.78
PARAFFINIC WAX	0.50	0.24
WOOD RESIN	1.00	0.49
ANTIOXIDANT 6PPD	1.00	0.49
ZINC OXIDE	5.00	2.44
ACCELERATOR TMTD	0.80	0.39
ACCELERATOR CBS	1.20	0.59
SULFUR	1.60	0.78
TOTAL	205.10	100.00

Properties	Method	Typical Value
Tc90 @150°C (min)	ASTM D5289	3.5
Physical Properties (Cured @ 150°C/Tc90+2 min)
300% Modulus (MPa)	ASTM D412	8.7
Tensile Strength (MPa)	ASTM D412	12.5
Elongation @ Break (%)	ASTM D412	443
Hardness (Shore A)	ASTM D2240	52

VIBROMOUNT-SHORE(A)45

Ingredient	PHR	%
BUTYL IMPRAMER R 1675	90.00	36.14
POLYCHLOROPRENE-LOW CRYSTALINITY( W MODIFIED)	10.00	4.02
CARBON FEF N550	50.00	20.08
CALCIUM CARBONATE	50.00	20.08
PARAFFINIC OIL	25.00	10.04
DOP	10.00	4.02
PEG400	2.00	0.80
PARAFFINIC WAX	1.00	0.40
ZINC OXIDE	5.00	2.01
STEARIC ACID	1.00	0.40
ACCELERATOR CBS	1.50	0.60
ACCELERATOR MBTS	0.50	0.20
ACCELERATOR TMTD	1.50	0.60
ACCELERATOR ZDBC	0.50	0.20
SULFUR	1.00	0.40
TOTAL	249.00	100.00

Properties	Method	Typical Value
Tc90 @170°C (min)	ASTM D5289	9.0
Physical Properties (Cured @ 170°C/Tc90+2 min)
300% Modulus (MPa)	ASTM D412	3.1
Tensile Strength (MPa)	ASTM D412	7.3
Elongation @ Break (%)	ASTM D412	729
Hardness (Shore A)	ASTM D2240	45
Rebound Resilience (Cured @ 170°C/Tc90+5 min)
Rebound Resilience @25°C (%)	ISO 4662	34

VIBROMOUNT-SHORE(A)35

Ingredient	PHR	%
BUTYL IMPRAMER R 1675	90.00	35.71
POLYCHLOROPRENE-LOW CRYSTALINITY( W MODIFIED)	10.00	3.97
CARBON FEF N550	35.00	13.89
CALCIUM CARBONATE	65.00	25.79
PARAFFINIC OIL	28.00	11.11
DOP	10.00	3.97
PEG400	2.00	0.79
PARAFFINIC WAX	1.00	0.40
ZINC OXIDE	5.00	1.98
STEARIC ACID	1.00	0.40
ACCELERATOR CBS	1.50	0.60
ACCELERATOR MBTS	0.50	0.20
ACCELERATOR TMTD	1.50	0.60
ACCELERATOR ZDBC	0.50	0.20
SULPHUR	1.00	0.40
TOTAL	252.00	100.00

Properties	Method	Typical Value
Tc90 @170°C (min)	ASTM D5289	9.0
Physical Properties (Cured @ 170°C/Tc90+2 min)
300% Modulus (MPa)	ASTM D412	2.6
Tensile Strength (MPa)	ASTM D412	7.1
Elongation @ Break (%)	ASTM D412	751
Hardness (Shore A)	ASTM D2240	35
Rebound Resilience (Cured @ 170°C/Tc90+5 min)
Rebound Resilience @25°C (%)	ISO 4662	34

SQUASH BALL

Ingredient	PHR	%
BROMOBUTYL IMPRAMER B2232	70.00	33.96
NR (RSS 4)	30.00	14.56
PPT SILICA (ZC185)	40.00	19.41
BARYATES	40.00	19.41
NAPHTHENIC OIL	10.00	4.85
DEG	2.00	0.97
NON STAINING ANTI-OXIDANT	1.00	0.49
ZINC OXIDE	10.00	4.85
ACCELERATOR CBS	1.50	0.73
ACCELERATOR TMTD	1.00	0.49
SULFUR	0.60	0.29
TOTAL	206.10	100.00

Properties	Method	Typical Value
Tc90 @140°C (min)	ASTM D5289	6.0
Physical Properties (Cured @ 140°C/Tc90+2 min)
300% Modulus (MPa)	ASTM D412	3.3
Tensile Strength (MPa)	ASTM D412	12.7
Elongation @ Break (%)	ASTM D412	861
Hardness (Shore A)	ASTM D2240	55
Rebound Resilience (Cured @ 140°C/Tc90+5 min)
Rebound Resilience @25°C (%)	ISO 4662	27

PHARMA STOPPER-SILICA

Ingredient	PHR	%
BROMOBUTYL IMPRAMER B2232	100.00	60.20
MAGNESIUM OXIDE	0.10	0.06
SILICA	55.00	33.11
LOW DENSITY POLYETHENE	5.00	3.01
STEARIC ACID	1.00	0.60
ZINC OXIDE	2.00	1.20
ACCELERATOR TBzTD	1.00	0.60
ACCELERATOR MBTS	1.50	0.90
SULFUR	0.50	0.30
TOTAL	166.10	100.00

Properties	Method	Typical Value
Tc90 @170°C (min)	ASTM D5289	9.0
Physical Properties (Cured @ 170°C/Tc90+2 min)
300% Modulus (MPa)	ASTM D412	3.2
Tensile Strength (MPa)	ASTM D412	14.3
Elongation @ Break (%)	ASTM D412	837
Hardness (Shore A)	ASTM D2240	50

PHARMA STOPPER-ZINC FREE

Ingredient	PHR	%
BROMOBUTYL IMPRAMER B2232	100.00	55.71
MAGNESIUM OXIDE	2.00	1.11
CALCINED CLAY	70.00	39.00
LOW DENSITY POLYETHENE	5.00	2.79
STEARIC ACID	1.00	0.56
VULTAC 3	1.50	0.84
TOTAL	179.50	100.00

Properties	Method	Typical Value
Tc90 @180°C (min)	ASTM D5289	17.0
Physical Properties (Cured @ 180°C/Tc90+2 min)
300% Modulus (MPa)	ASTM D412	1.9
Tensile Strength (MPa)	ASTM D412	9.6
Elongation @ Break (%)	ASTM D412	980
Hardness (Shore A)	ASTM D2240	43

BALL BLADDER- COLORED

Ingredient	PHR	%
STYLAMER SBR-1502	30.00	15.11
NR (RSS4)	30.00	15.11
BROMOBUTYL IMPRAMER B2232	40.00	20.14
CALCINED CLAY	20.00	10.07
PPT SILICA (ZC185)	40.00	20.14
MINERAL FILLER-VAPORLINK	10.00	5.04
NAPHTHENIC OIL	10.00	5.04
SP OIL	1.00	0.50
PF RESIN	2.00	1.01
PARAFFINIC WAX	2.00	1.01
TITANIUM OXIDE	2.00	1.01
COLOR PIGMENT	2.00	1.01
STEARIC ACID	2.00	1.01
ZINC OXIDE	4.00	2.01
ACCELERATOR TMTD	0.50	0.25
ACCELERATOR MBTS	1.50	0.76
ANTI-SCORCH PVI	0.10	0.05
SULFUR	1.50	0.76
TOTAL	198.60	100.00

Properties	Method	Typical Value
Tc90 @160°C (min)	ASTM D5289	5.0
Physical Properties (Cured @ 160°C/Tc90+2 min)
300% Modulus (MPa)	ASTM D412	7.3
Tensile Strength (MPa)	ASTM D412	12.7
Elongation @ Break (%)	ASTM D412	655
Hardness (Shore A)	ASTM D2240	63
Air retention Properties (Cured @ 160°C/Tc90+2 min)
Air permeability (cc-mm/[m2-day])	ASTM D3985	293

BALL BLADDER-BLACK

Ingredient	PHR	%
STYLAMER SBR-1502	30.00	15.42
NR (RSS4)	30.00	15.42
BROMOBUTYL IMPRAMER B2232	40.00	20.55
CARBON FEF N550	40.00	20.55
CALCIUM CARBONATE	10.00	5.14
PPT SILICA ( ZC185)	10.00	5.14
MINERAL FILLER-VAPORLINK	10.00	5.14
NAPHTHENIC OIL	10.00	5.14
PARAFFINIC WAX	2.00	1.03
PF RESIN	2.00	1.03
ANTIOXIDANT TDQ	1.00	0.51
STEARIC ACID	2.00	1.03
ZINC OXIDE	4.00	2.06
ACCELERATOR TMTD	0.50	0.26
ACCELERATOR MBTS	1.50	0.77
ANTI-SCORCH PVI	0.10	0.05
SULFUR	1.50	0.77
TOTAL	194.60	100.00

Properties	Method	Typical Value
Tc90 @160°C (min)	ASTM D5289	3.0
Physical Properties (Cured @ 160°C/Tc90+2 min)
300% Modulus (MPa)	ASTM D412	10.9
Tensile Strength (MPa)	ASTM D412	13.5
Elongation @ Break (%)	ASTM D412	394
Hardness (Shore A)	ASTM D2240	59
Air retention properties (Cured @ 160°C/Tc90+2 min)
Air permeability (cc-mm/[m2-day])	ASTM 3985	231

HIGH TEMPERATURE HOSE

Ingredient	PHR	%
BROMOBUTYL IMPRAMER B2232	100.00	58.48
CARBON FEF N550	50.00	29.24
PPT SILICA (ZC 185)	5.00	2.92
PARAFFINIC OIL	7.00	4.09
STEARIC ACID	1.00	0.58
ACCELERATOR MBTS	2.00	1.17
ACCELERATOR TMTD	1.00	0.58
ZINC OXIDE	5.00	2.92
TOTAL	171.00	100.00

Properties	Method	Typical Value
Tc90 @160°C (min)	ASTM D5289	4.0
Physical Properties (Cured @ 160°C/Tc90+2 min)
300% Modulus (MPa)	ASTM D412	4.3
Tensile Strength (MPa)	ASTM D412	11.1
Elongation @ Break (%)	ASTM D412	701
Hardness (Shore A)	ASTM D2240	45

RICE POLISHER BRAKE- PREMIUM: RPB 3

Ingredient	PHR	%
NATURAL RUBBER (RMA 4/SMR 20)	50.00	18.4
CISAMER 01	50.00	18.4
PEPTISER	0.25	0.1
CI Resin	2.00	0.7
STEARIC ACID	2.50	0.9
TITANIUM DIOXIDE	1.30	0.5
ZINC OXIDE	9.00	3.3
CHINA CLAY	105.00	38.6
SPINDLE OIL	20.00	7.4
ANTIOXIDANT SP	1.50	0.6
PPT SILICA VN3	11.00	4.0
ALUMINIUM SILICATE	14.00	5.1
DEG	1.10	0.4
ACCELERATOR CBS	1.50	0.6
ACCELERATOR TMT	0.15	0.1
SULFUR	2.80	1.0
TOTAL	272.10	100.00

Properties	Method	Typical Value
Tc90 @140°C (min)	ASTM D5289	12.5
Physical Properties (Cured @ 140°C/Tc90+2 min)
300% Modulus (MPa)	ASTM D412	4.7
Tensile Strength (MPa)	ASTM D412	12.1
Elongation @ Break (%)	ASTM D412	723
Hardness (Shore A)	ASTM D2240	61
Specific gravity	ASTM D297	1.37
Abrasion Properties (Cured @ 140°C/Tc90+5 min)
ARI	ASTM D5963	85
Abrasion Loss (mm³)	ASTM D5963	175

RICE POLISHER BRAKE- PREMIUM: RPB 2

Ingredient	PHR	%
NATURAL RUBBER (RMA 4/SMR 20)	40.0	14.7
CISAMER 01	60.0	22.1
PEPTISER	0.2	0.1
CI Resin	2.0	0.7
STEARIC ACID	2.5	0.9
TITANIUM DIOXIDE	1.3	0.5
ZINC OXIDE	9.0	3.3
CHINA CLAY	105.0	38.6
SPINDLE OIL	20.0	7.4
ANTIOXIDANT SP	1.5	0.6
PPT SILICA VN3	11.0	4.0
ALUMINIUM SILICATE	14.0	5.1
DEG	1.10	0.4
ACCELERATOR CBS	1.50	0.6
ACCELERATOR TMT	0.15	0.1
SULFUR	2.80	1.0
TOTAL	272.05	100.00

Properties	Method	Typical Value
Tc90 @140°C (min)	ASTM D5289	13.0
Physical Properties (Cured @ 140°C/Tc90+2 min)
300% Modulus (MPa)	ASTM D412	4.4
Tensile Strength (MPa)	ASTM D412	11.2
Elongation @ Break (%)	ASTM D412	695
Hardness (Shore A)	ASTM D2240	61
Specific gravity	ASTM D297	1.38
Abrasion Properties (Cured @ 140°C/Tc90+5 min)
ARI	ASTM D5963	89
Abrasion Loss (mm³)	ASTM D5963	168

RICE POLISHER BRAKE- PREMIUM: RPB 1

Ingredient	PHR	%
NATURAL RUBBER (RMA 4/SMR 20)	30.0	11.0
CISAMER 01	70.0	25.7
PEPTISER	0.2	0.1
CI Resin	2.0	0.7
STEARIC ACID	2.5	0.9
TITANIUM DIOXIDE	1.3	0.5
ZINC OXIDE	9.0	3.3
CHINA CLAY	105.0	38.6
SPINDLE OIL	20.0	7.4
ANTIOXIDANT SP	1.5	0.6
PPT SILICA VN3	11.0	4.0
ALUMINIUM SILICATE	14.0	5.1
DEG	1.10	0.4
ACCELERATOR CBS	1.50	0.6
ACCELERATOR TMT	0.15	0.1
SULFUR	2.80	1.0
TOTAL	272.00	100.00

Properties	Method	Typical Value
Tc90 @140°C (min)	ASTM D5289	14.5
Physical Properties (Cured @ 140°C/Tc90+2 min)
300% Modulus (MPa)	ASTM D412	4.4
Tensile Strength (MPa)	ASTM D412	13.1
Elongation @ Break (%)	ASTM D412	707
Hardness (Shore A)	ASTM D2240	59
Specific gravity	ASTM D297	1.38
Abrasion Properties (Cured @ 140°C/Tc90+5 min)
ARI	ASTM D5963	96
Abrasion Loss (mm³)	ASTM D5963	155

RICE POLISHER BRAKE- COMMERCIAL: RPB 3

Ingredient	PHR	%
NATURAL RUBBER (RMA 4/SMR 20)	50.00	13.2
CISAMER 01	50.00	13.2
PEPTISER	0.25	0.1
CI Resin	2.00	0.5
STEARIC ACID	2.50	0.7
TITANIUM DIOXIDE	1.30	0.3
ZINC OXIDE	9.00	2.4
CHINA CLAY	210.00	55.5
SPINDLE OIL	35.00	9.3
ANTIOXIDANT SP	1.50	0.4
PPT SILICA VN3	11.00	2.9
DEG	1.10	0.3
ACCELERATOR CBS	1.50	0.4
ACCELERATOR TMT	0.15	0.04
SULFUR	2.80	0.7
TOTAL	378.10	100.00

Properties	Method	Typical Value
Tc90 @140°C (min)	ASTM D5289	17.5
Physical Properties (Cured @ 140°C/Tc90+2 min)
300% Modulus (MPa)	ASTM D412	5.2
Tensile Strength (MPa)	ASTM D412	8.9
Elongation @ Break (%)	ASTM D412	536
Hardness (Shore A)	ASTM D2240	63
Specific gravity	ASTM D297	1.52
Abrasion Properties (Cured @ 140°C/Tc90+5 min)
ARI	ASTM D5963	67
Abrasion Loss (mm³)	ASTM D5963	223

RICE POLISHER BRAKE- COMMERCIAL: RPB 2

Ingredient	PHR	%
NATURAL RUBBER (RMA 4/SMR 20)	40.00	10.6
CISAMER 01	60.00	15.9
PEPTISER	0.20	0.1
CI Resin	2.00	0.5
STEARIC ACID	2.50	0.7
TITANIUM DIOXIDE	1.30	0.3
ZINC OXIDE	9.00	2.4
CHINA CLAY	210.00	55.5
SPINDLE OIL	35.00	9.3
ANTIOXIDANT SP	1.50	0.4
PPT SILICA VN3	11.00	2.9
DEG	1.10	0.3
ACCELERATOR CBS	1.50	0.4
ACCELERATOR TMT	0.15	0.04
SULFUR	2.80	0.7
TOTAL	378.05	100.00

Properties	Method	Typical Value
Tc90 @140°C (min)	ASTM D5289	19.0
Physical Properties (Cured @ 140°C/Tc90+2 min)
300% Modulus (MPa)	ASTM D412	4.9
Tensile Strength (MPa)	ASTM D412	7.8
Elongation @ Break (%)	ASTM D412	517
Hardness (Shore A)	ASTM D2240	61
Specific gravity	ASTM D297	1.51
Abrasion Properties (Cured @ 140°C/Tc90+5 min)
ARI	ASTM D5963	72
Abrasion Loss (mm³)	ASTM D5963	207

RICE POLISHER BRAKE- COMMERCIAL: RPB 1

Ingredient	PHR	%
NATURAL RUBBER (RMA 4/SMR 20)	30.00	7.9
CISAMER 01	70.00	18.5
PEPTISER	0.15	0.04
CI Resin	2.00	0.5
STEARIC ACID	2.50	0.7
TITANIUM DIOXIDE	1.30	0.3
ZINC OXIDE	9.00	2.4
CHINA CLAY	210.00	55.6
SPINDLE OIL	35.00	9.3
ANTIOXIDANT SP	1.50	0.4
PPT SILICA VN3	11.00	2.9
DEG	1.10	0.3
ACCELERATOR CBS	1.50	0.4
ACCELERATOR TMT	0.15	0.04
SULFUR	2.80	0.7
TOTAL	378.00	100.00

Properties	Method	Typical Value
Tc90 @140°C (min)	ASTM D5289	19.0
Physical Properties (Cured @140°C/Tc90+2 min)
300% Modulus (MPa)	ASTM D412	4.3
Tensile Strength (MPa)	ASTM D412	8.0
Elongation @ Break (%)	ASTM D412	600
Hardness (Shore A)	ASTM D2240	59
Specific gravity	ASTM D297	1.51
Abrasion Properties (Cured @140°C/Tc90+5 min)
ARI	ASTM D5963	78
Abrasion Loss (mm³)	ASTM D5963	191

RICE DEHUSK ROLLER

Ingredient	PHR	%
NBR (MID ACN)	87.5	40.93
CISAMER 01	12.5	5.85
CHLOROPRENE RUBBER	5.0	2.34
STEARIC ACID	1.5	0.70
ZINC OXIDE	8.0	3.74
THERMOSET RESIN	20.0	9.35
ULTRASIL - VN3 (SILICA)	65.00	30.40
ANTIOXIDANT TQ	2.0	0.94
PLASTIZER (DOP)	7.0	3.27
DEG	2.0	0.94
SULFUR	2.0	0.94
ACCELERATOR CBS	1.3	0.61
TOTAL	213.8	100.00

Properties	Method	Typical Value
tc90 @150°C / 60 min (min)	ASTM D5289	37.1
Physical Properties (Cured @ 150°C / Tc90+2 Min)
300% Modulus (MPa)	ASTM D412	14.2
Tensile Strength (MPa)	ASTM D412	20.8
Elongation @ Break (%)	ASTM D412	480
Hardness (Shore A)	ASTM D2240	86
Specific gravity	ASTM D297	1.37
Abrasion Properties (Cured @ 150°C / Tc90+2 Min)
Abrasion Loss (mm³)	ASTM D5963	92.5
Cut & Chip Properties (Cured @ 150°C / Tc90+2 Min)
Mass loss (gm)	Vendor method	0.99

validate the information in their plant, process, products and its intended application before implementation. Trade names, if any, used are only for information and in no way promoting the specific material. Reliance Industries Limited disclaim liability for any loss, direct or indirect injury suffered , or damage incurred as a result of above information/this document.

Conveyor cover-High Tensile (M24) : CCV 1

Ingredient	PHR	%
STYLAMER SBR-1502	100.00	57.27
CARBON HAF-HS N339	55.00	31.50
AROMATIC OIL	6.00	3.44
PF RESIN	1.00	0.57
ANTIOXIDANT TQ	2.00	1.15
ANTIOXIDANT 6PPD	1.00	0.57
STEARIC ACID	2.00	1.15
ZINC OXIDE	5.00	2.86
ACCELERATOR TBBS	1.20	0.69
SULFUR	1.40	0.80
TOTAL	174.60	100.00

Properties	Method	Typical Value
Tc90 @160°C (min)	ASTM D5289	12.5
Physical Properties (Cured @160°C/Tc90+2 min)
300% Modulus (MPa)	ASTM D412	13.2
Tensile Strength (MPa)	ASTM D412	25.9
Elongation @ Break (%)	ASTM D412	515
Hardness (Shore A)	ASTM D2240	64
Abrasion Properties (Cured @160°C/Tc90+5 min)
Abrasion Loss (mm³)	ASTM D5963	106
Percentage Retention - 70°C, 7 days
Tensile Strength (%)	ASTM D412	97
Elongation @ Break (%)	ASTM D412	76

Conveyor cover-Low Rolling Resistance : CCV 2

Ingredient	PHR	%
NATURAL RUBBER (RSS 4)	40.00	25.32
CISAMER-01	60.00	37.97
PPT SILICA VN3	12.00	7.59
CARBON HAF-HS N339	33.00	20.89
AROMATIC OIL	2.00	1.27
ANTIOXIDANT TQ	1.00	0.63
ANTIOXIDANT 6PPD	1.00	0.63
STEARIC ACID	2.00	1.27
ZINC OXIDE	4.00	2.53
ACCELERATOR CBS	1.50	0.95
SULFUR	1.50	0.95
TOTAL	158.00	100.00

Properties	Method	Typical Value
Tc90 @160°C (min)	ASTM D5289	5.0
Physical Properties (Cured @160°C/ Tc90+2 min)
300% Modulus (MPa)	ASTM D412	7.4
Tensile Strength (MPa)	ASTM D412	19.7
Elongation @ Break (%)	ASTM D412	555
Hardness (Shore A)	ASTM D2240	58
Dynamic Properties (Cured @160°C/Tc90+2 min)- 2% dynamic strain, 10Hz - Tension Mode
E' @ 0°C (MPa)	ASTM D5992	5.29
E" @ 0°C (MPa)	ASTM D5992	0.88
RRF-E"/(E')^4/3	ASTM D5992	0.095

CONVEYOR COVER-SUPER LOW RR : CCV 3

Ingredient	PHR	%
NATURAL RUBBER (RSS 4)	40.00	25.81
CISAMER-1220	60.00	38.71
PPT SILICA VN3	12.00	7.74
CARBON HAF-HS N339	30.00	19.35
AROMATIC OIL	2.00	1.29
ANTIOXIDANT 6PPD	1.00	0.65
ANTIOXIDANT TQ	1.00	0.65
STEARIC ACID	2.00	1.29
ZINC OXIDE	4.00	2.58
ACCELERATOR CBS	1.50	0.97
SOLUBLE SULFUR	1.50	0.97
TOTAL	155.00	100.00

Properties	Method	Typical Value
Tc90 @160°C (min)	ASTM D5289	5.5
Physical Properties (Cured @160°C/Tc90+2 Min)
300% Modulus (MPa)	ASTM D412	8.7
Tensile Strength (MPa)	ASTM D412	19.7
Elongation @ Break (%)	ASTM D412	511
Hardness (Shore A)	ASTM D2240	60
Dynamic Properties (Cured @160°C/Tc90+2 Min)- 2% Dynamic Strain, 10Hz - Tension Mode
E' @0°C (MPa)	ASTM D5992	6.3
E" @0°C (MPa)	ASTM D5992	1.06
RRF-E"/(E')^4/3	ASTM D5992	0.08

CONVEYOR COVER N17-OE SBR : CCV4

Ingredient	PHR	%
NATURAL RUBBER (RSS 4)	30.00	15.34
STYLAMER-SBR 1712	41.25	21.09
CISAMER-01	40.00	20.46

CARBON ISAF N220	62.00	31.71
AROMATIC OIL	8.00	4.09
MC WAX	1.00	0.51
PF RESIN	2.00	1.02
STEARIC ACID	2.50	1.28
ZINC OXIDE	4.00	2.05
ANTIOXIDANT 6PPD	1.00	0.51
ANTIOXIDANT TQ	0.50	0.26
ACCELERATOR CBS	1.25	0.64
ACCELERATOR TMT	0.15	0.08
SOLUBLE SULFUR	1.90	0.97
TOTAL	195.55	100.00

Properties	Method	Typical Value
Tc90 @150°C (min)	ASTM D5289	14.0
Physical Properties (Cured @150°C/Tc90+2 Min)
300% Modulus (MPa)	ASTM D412	8.4
Tensile Strength (MPa)	ASTM D412	19.5
Elongation @ Break (%)	ASTM D412	550
Hardness (Shore A)	ASTM D2240	62
Abrasion Properties (Cured @150⁰C/Tc90+5 Min)
Abrasion loss (mm³)	ASTM D5963	68

CONVEYOR COVER N17-OE SBR : CCV5

Ingredient	PHR	%
STYLAMER-SBR 1712	110.00	42.02
CISAMER-01	20.00	7.64
RECLAIM RUBBER	40.00	15.28

CARBON ISAF-HS N234	80.00	30.56
STEARIC ACID	2.00	0.76
ZINC OXIDE	3.00	1.15
MC WAX	1.50	0.57
ANTIOXIDANT 6PPD	1.00	0.38
ANTIOXIDANT TQ	1.00	0.38
ACCELERATOR TBBS	1.00	0.38
ACCELERATOR TMT	0.30	0.11
SOLUBLE SULFUR	2.00	0.76
TOTAL	261.80	100.00

Properties	Method	Typical Value
Tc90 @150°C (min)	ASTM D5289	12.0
Physical Properties (Cured @150°C/Tc90+2 Min)
300% Modulus (MPa)	ASTM D412	10.9
Tensile Strength (MPa)	ASTM D412	19
Elongation @ Break (%)	ASTM D412	480
Hardness (Shore A)	ASTM D2240	63
Abrasion Properties (Cured @150⁰C/Tc90+5 Min)
Abrasion loss (mm³)	ASTM D5963	88

CONVEYOR PLY COMPOUND : CCP1

Ingredient	PHR	%
ISNR 20	25.00	10.16
STYLAMER-SBR 1712	55.00	22.35
RECLAIM RUBBER	70.00	28.44
CARBON GPF N660	45.00	18.29
CHINA CLAY	30.00	12.19
RUBBER CRUMB	8.00	3.25
STEARIC ACID	1.50	0.61
ZINC OXIDE	4.00	1.63
PF RESIN	3.00	1.22
ANTIOXIDANT TQ	1.00	0.41
ACCELERATOR CBS	0.80	0.33
ACCELERATOR MBTS	0.30	0.12
SOLUBLE SULFUR	2.50	1.02
TOTAL	246.10	100.00

Properties	Method	Typical Value
Tc90 @150°C (min)	ASTM D5289	12.8
Physical Properties (Cured @150°C/Tc90+2 Min)
300% Modulus (MPa)	ASTM D412	8.5
Tensile Strength (MPa)	ASTM D412	11.4
Elongation @ Break (%)	ASTM D412	390
Hardness (Shore A)	ASTM D2240	59
Peel adhesion testing: - Test speed: 50 mm/min (cured @ 150⁰C for 15 min)
Peel adhesion force (N/mm)	ASTM D5963	7.0

CONVEYOR PLY COMPOUND : CCP2

Ingredient	PHR	%
ISNR 20	25.00	10.16
STYLAMER-SBR 1739	55.00	22.35
RECLAIM RUBBER	70.00	28.44
CARBON GPF N660	45.00	18.29
CHINA CLAY	30.00	12.19
RUBBER CRUMB	8.00	3.25
STEARIC ACID	1.50	0.61
ZINC OXIDE	4.00	1.63
PF RESIN	3.00	1.22
ANTIOXIDANT TQ	1.00	0.41
ACCELERATOR CBS	0.80	0.33
ACCELERATOR MBTS	0.30	0.12
SOLUBLE SULFUR	2.50	1.02
TOTAL	246.10	100.00

Properties	Method	Typical Value
Tc90 @150°C (min)	ASTM D5289	13.0
Physical Properties (Cured @150°C/Tc90+2 Min)
300% Modulus (MPa)	ASTM D412	9.0
Tensile Strength (MPa)	ASTM D412	11.9
Elongation @ Break (%)	ASTM D412	400
Hardness (Shore A)	ASTM D2240	60
Peel adhesion testing: - Test speed: 50 mm/min (cured @ 150⁰C for 15 min)
Peel adhesion force (N/mm)	ASTM D5963	7.4

Conveyor PIPS

Ingredient	PHR	%
NATURAL RUBBER (RSS 4)	35.00	18.25
CISAMER-01	65.00	33.89
CARBON FEF N550	70.00	36.50
AROMATIC OIL	7.00	3.65
ANTIOXIDANT TMQ	2.00	1.04
ANTIOXIDANT DPPD	2.00	1.04
ZINC OXIDE	5.00	2.61
STEARIC ACID	2.50	1.30
ACCELERATOR CBS	1.80	0.94
SULFUR	1.50	0.78
TOTAL	191.80	100.00

Properties	Method	Typical Value
Tc90 @185°C (min)	ASTM D5289	1.1
Physical Properties (Cured @185°C/Tc90+1 min)
300% Modulus (MPa)	ASTM D412	2.4
Tensile Strength (MPa)	ASTM D412	14.8
Elongation @ Break (%)	ASTM D412	475
Hardness (Shore A)	ASTM D2240	61
Rebound Resilience (Cured @185°C/Tc90+5 min)
Rebound Resilience @25°C (%)	ISO 4662	48
Compression Set Properties-24 hrs @70°C (Cured @185°C/Tc90+5 min)
Compression Set (%)	ASTM D395	6

Precured tread- Light Commercial : PCTR 1

Ingredient	PHR	%
STYLAMER SBR-1502	70.00	38.02
CISAMER-01	30.00	16.30
CARBON ISAF-HS N234	45.00	24.44
PPT SILICA VN3	15.00	8.15
AROMATIC OIL	10.00	5.43
MC WAX/WAX BLEND	1.00	0.54
ANTIOXIDANT 6PPD	0.50	0.27
ANTIOXIDANT TDQ	1.00	0.54
STEARIC ACID	2.00	1.09
ZINC OXIDE	4.00	2.17
PF RESIN	2.00	1.09
ACCELERATOR TBBS	1.20	0.65
ACCELERATOR DPG	0.50	0.27
SULFUR	1.90	1.03
TOTAL	184.10	100.00

Properties	Method	Typical Value
Tc90 @145°C (min)	ASTM D5289	26.0
Physical Properties (Cured @145°C/Tc90+2 min)
300% Modulus (MPa)	ASTM D412	9.0
Tensile Strength (MPa)	ASTM D412	19.3
Elongation @ Break (%)	ASTM D412	509
Hardness (Shore A)	ASTM D2240	64
Abrasion Properties (Cured @145°C/Tc90+5 min)
Abrasion Resistance Index (ARI)	ASTM D5963	140
Heat Build Up Properties (Cured @145°C/Tc90+5 Min) - 30Hz, 100°C, 7kg, 25 min
HBU (°C)	ASTM D623	28

Precured tread- Light Commercial : PCTR 2

Ingredient	PHR	%
STYLAMER SBR-1712	96.25	44.28
CISAMER-01	30.00	13.80
CARBON ISAF-HS N234	55.00	25.30
PPT SILICA VN3	15.00	6.90
AROMATIC OIL	7.00	3.22
MC WAX/WAX BLEND	1.00	0.46
ANTIOXIDANT 6PPD	0.50	0.23
ANTIOXIDANT TDQ	1.00	0.46
STEARIC ACID	2.00	0.92
ZINC OXIDE	4.00	1.84
PF RESIN	2.00	0.92
ACCELERATOR TBBS	1.20	0.55
ACCELERATOR DPG	0.50	0.23
SULFUR	1.90	0.87
TOTAL	217.35	100.00

Properties	Method	Typical Value
Tc90 @145°C (min)	ASTM D5289	28.0
Physical Properties (Cured @145°C/Tc90+2 min)
300% Modulus (MPa)	ASTM D412	6.0
Tensile Strength (MPa)	ASTM D412	18.7
Elongation @ Break (%)	ASTM D412	610
Hardness (Shore A)	ASTM D2240	58
Abrasion Properties (Cured @145°C/Tc90+5 min)
Abrasion Resistance Index (ARI)	ASTM D5963	113
Heat Build Up Properties (Cured @145°C/Tc90+5 Min) - 30Hz, 100°C, 7kg, 25 min
HBU (°C)	ASTM D623	26

Precured tread- Light Commercial : PCTR 3

Ingredient	PHR	%
NATURAL RUBBER (RMA 4/SMR 20)	20.00	10.78
STYLAMER SBR-1712	55.00	29.65
CISAMER 01	40.00	21.56
CARBON ISAF N220	50.00	26.95
AROMATIC OIL	7.50	4.04
ANTIOXIDANT TQ	1.00	0.54
ANTIOXIDANT 6PPD	1.00	0.54
MC WAX	1.00	0.54
ZINC OXIDE	4.00	2.16
STEARIC ACID	2.50	1.35
ACCELERATOR MBS	1.20	0.65
SULFUR	2.30	1.24
TOTAL	185.50	100.00

Properties	Method	Typical Value
Tc90 @145°C (Min)	ASTM D5289	25.0
Physical Properties (Cured @145°C/Tc90+2 Min)
300% Modulus (MPa)	ASTM D412	8.9
Tensile Strength (MPa)	ASTM D412	15.4
Elongation @ Break (%)	ASTM D412	448
Hardness (Shore A)	ASTM D2240	62
Abrasion Properties (Cured @145°C/Tc90+5 Min)
Abrasion Resistance Index (ARI)	ASTM D5963	150
Heat Build Up Properties (Cured @145°C/Tc90+5 Min) - 30Hz, 100°C, 7kg, 25 min
HBU (°C)	ASTM D623	20

Precured tread- Truck & Bus Bias : PCTR 4

Ingredient	PHR	%
NATURAL RUBBER (RSS 4)	35.00	18.34
STYLAMER SBR-1502	35.00	18.34
CISAMER-01	30.00	15.72
CARBON ISAF N220	55.00	28.83
PPT SILICA VN3	10.00	5.24
HOMOGENISER	2.00	1.05
AROMATIC OIL	10.00	5.24
MC WAX/WAX BLEND	1.00	0.52
ANTIOXIDANT 6PPD	0.50	0.26
ANTIOXIDANT TDQ	1.00	0.52
STEARIC ACID	2.00	1.05
ZINC OXIDE	4.00	2.10
PF RESIN	2.00	1.05
ACCELERATOR TBBS	1.00	0.52
ACCELERATOR DPG	0.30	0.16
SULFUR	2.00	1.05
TOTAL	190.80	100.00

Properties	Method	Typical Value
Tc90 @160°C (min)	ASTM D5289	14.0
Physical Properties (Cured @ 160°C/Tc90+2 min)
300% Modulus (MPa)	ASTM D412	9.5
Tensile Strength (MPa)	ASTM D412	20.3
Elongation @ Break (%)	ASTM D412	499
Hardness (Shore A)	ASTM D2240	67
Angle Tear (Kgs/mm)	ASTM D624	6.0
Abrasion Properties (Cured @160°C/Tc90+5 min)
Abrasion Resistane Index (ARI)	ASTM D5963	208.0
Heat Build Up Properties (Cured @145°C/Tc90+5 Min) - 30Hz, 100°C, 7kg, 25 min
HBU (°C)	ASTM D623	26

Precured tread- Truck & Bus Bias : PCTR 5

Ingredient	PHR	%
NATURAL RUBBER (RSS 4)	35.00	16.36
STYLAMER SBR-1712	48.13	22.50
CISAMER-01	30.00	14.02
CARBON ISAF N220	65.00	30.38
PPT SILICA VN3	10.00	4.67
HOMOGENISER	2.00	0.93
AROMATIC OIL	10.00	4.67
MC WAX/WAX BLEND	1.00	0.47
ANTIOXIDANT 6PPD	0.50	0.23
ANTIOXIDANT TDQ	1.00	0.47
STEARIC ACID	2.00	0.93
ZINC OXIDE	4.00	1.87
PF RESIN	2.00	0.93
ACCELERATOR TBBS	1.00	0.47
ACCELERATOR DPG	0.30	0.14
SULFUR	2.00	0.93
TOTAL	213.93	100.00

Properties	Method	Typical Value
Tc90 @160°C (min)	ASTM D5289	13.7
Physical Properties (Cured @ 160°C/Tc90+2 min)
300% Modulus (MPa)	ASTM D412	8.7
Tensile Strength (MPa)	ASTM D412	18.3
Elongation @ Break (%)	ASTM D412	526
Hardness (Shore A)	ASTM D2240	66
Angle Tear (Kgs/mm)	ASTM D624	6.0
Abrasion Properties (Cured @160°C/Tc90+5 min)
Abrasion Resistane Index (ARI)	ASTM D5963	188.0
Heat Build Up Properties (Cured @145°C/Tc90+5 Min) - 30Hz, 100°C, 7kg, 25 min
HBU (°C)	ASTM D623	27

Precured tread- Truck & Bus Bias : PCTR 6

Ingredient	PHR	%
NATURAL RUBBER (RSS 4)	35.00	18.54
STYLAMER SBR-1502	30.00	15.89
CISAMER-01	35.00	18.54
CARBON HAF-HS N339	55.00	29.13
PPT SILICA VN3	10.00	5.30
HOMOGENISER	2.00	1.06
AROMATIC OIL	8.00	4.24
MC WAX/WAX BLEND	1.00	0.53
ANTIOXIDANT 6PPD	0.50	0.26
ANTIOXIDANT TDQ	1.00	0.53
STEARIC ACID	2.00	1.06
ZINC OXIDE	4.00	2.12
PF RESIN	2.00	1.06
ACCELERATOR TBBS	1.00	0.53
ACCELERATOR DPG	0.30	0.16
SULFUR	2.00	1.06
TOTAL	188.80	100.00

Properties	Method	Typical Value
Tc90 @160°C (min)	ASTM D5289	12.0
Physical Properties (Cured @ 160°C/Tc90+2 min)
300% Modulus (MPa)	ASTM D412	12.5
Tensile Strength (MPa)	ASTM D412	20.1
Elongation @ Break (%)	ASTM D412	458
Hardness (Shore A)	ASTM D2240	69
Angle Tear (Kgs/mm)	ASTM D624	7.0
Abrasion Properties (Cured @160°C/Tc90+5 min)
Abrasion Resistane Index (ARI)	ASTM D5963	250
Heat Build Up Properties (Cured @145°C/Tc90+5 Min) - 30Hz, 100°C, 7kg, 25 min
HBU (°C)	ASTM D623	24

Precured tread- Truck & Bus Bias : PCTR 7

Ingredient	PHR	%
NATURAL RUBBER (RSS 4)	50.00	26.65
CISAMER-01	50.00	26.65
CARBON HAF-HS N339	60.00	31.98
AROMATIC OIL	14.00	7.46
ANTIOXIDANT TDQ	1.25	0.67
ANTIOXIDANT 6PPD	0.75	0.40
STEARIC ACID	2.50	1.33
ZINC OXIDE	4.00	2.13
CI RESIN	2.00	1.07
RETARDER PVI	0.10	0.05
ACCELERATOR MBS	1.50	0.80
SULFUR	1.50	0.80
TOTAL	187.60	100.00

Properties	Method	Typical Value
Tc90 @145°C (min)	ASTM D5289	22.9
Physical Properties (Cured @145°C/Tc90+2 Min)
300% Modulus (MPa)	ASTM D412	11.0
Tensile Strength (MPa)	ASTM D412	21.0
Elongation @ Break (%)	ASTM D412	508
Hardness (Shore A)	ASTM D2240	65
Tear Strength (N/mm)	ASTM D624	93
Abrasion Properties (Cured @145°C/Tc90+5 Min)
Abrasion Resistance Index (ARI)	ASTM D5963	148
Heat Build Up Properties (Cured @145°C/Tc90+5 Min) - 30Hz, 100°C, 7kg, 25 min
HBU (°C)	ASTM D623	29

PRECURED TREAD - TRUCK & BUS BIAS : PCTR 8

Ingredient	PHR	%
NATURAL RUBBER (RSS 4)	50.00	26.65
CISAMER-1220	50.00	26.65
CARBON HAF-HS N339	60.00	31.98
AROMATIC OIL	14.00	7.46
ANTIOXIDANT TDQ	1.25	0.67
ANTIOXIDANT 6PPD	0.75	0.40
STEARIC ACID	2.50	1.33
ZINC OXIDE	4.00	2.13
CI RESIN	2.00	1.07
RETARDER PVI	0.10	0.05
ACCELERATOR MBS	1.50	0.80
SULFUR	1.50	0.80
TOTAL	187.60	100.00

Properties	Method	Typical Value
Tc90 @145°C (min)	ASTM D5289	23.5
Physical Properties (Cured @145°C/Tc90+2 Min)
300% Modulus (MPa)	ASTM D412	11.2
Tensile Strength (MPa)	ASTM D412	21.0
Elongation @ Break (%)	ASTM D412	500
Hardness (Shore A)	ASTM D2240	65
Tear Strength (N/mm)	ASTM D624	90
Abrasion Properties (Cured @145°C/Tc90+5 Min)
Abrasion Resistance Index (ARI)	ASTM D5963	150
Heat Build Up Properties (Cured @145°C/Tc90+5 Min) - 30Hz, 100°C, 7kg, 25 min
HBU (°C)	ASTM D623	30

PRECURED TREAD - TRUCK & BUS BIAS : PCTR 9

Ingredient	PHR	%
NATURAL RUBBER (RSS 4)	50.00	26.65
CISAMER-51	50.00	26.65
CARBON HAF-HS N339	60.00	31.98
PROCESS OIL	14.00	7.46
ANTIOXIDANT TDQ	1.25	0.67
ANTIOXIDANT 6PPD	0.75	0.40
STEARIC ACID	2.50	1.33
ZINC OXIDE	4.00	2.13
CI RESIN	2.00	1.07
RETARDER PVI	0.10	0.05
ACCELERATOR MBS	1.00	0.53
SULFUR	2.00	1.07
TOTAL	187.60	100.00

Properties	Method	Typical Value
Tc90 @145°C (min)	ASTM D5289	23.2
Physical Properties (Cured @145°C/Tc90+2 Min)
300% Modulus (MPa)	ASTM D412	11.0
Tensile Strength (MPa)	ASTM D412	21.1
Elongation @ Break (%)	ASTM D412	501
Hardness (Shore A)	ASTM D2240	66
Tear Strength (N/mm)	ASTM D624	85
Abrasion Properties (Cured @145°C/Tc90+5 Min)
Abrasion Resistance Index (ARI)	ASTM D5963	158
Heat Build Up Properties (Cured @145°C/Tc90+5 Min) - 30Hz, 100°C, 7kg, 25 min
HBU (°C)	ASTM D623	29

PRECURED TREAD- TRUCK & BUS BIAS : PCTR 10

Ingredient	PHR	%
NATURAL RUBBER (RSS 4)	50.00	26.34
CISAMER-1220	50.00	26.34
CARBON ISAF-HS N234	60.00	31.61
AROMATIC OIL	17.00	8.96
MC WAX/WAX BLEND	1.00	0.53
ANTIOXIDANT TQ	1.00	0.53
ANTIOXIDANT 6PPD	1.00	0.53
STEARIC ACID	2.00	1.05
ZINC OXIDE	3.00	1.58
CI RESIN	2.00	1.05
RETARDER CTP	0.10	0.05
ACCELERATOR MBS	0.90	0.47
ACCELERATOR TMTD	0.02	0.01
SOLUBLE SULFUR	1.80	0.95
TOTAL	189.82	100.00

Properties	Method	Typical Value
Tc90 @150°C (min)	ASTM D5289	13.4
Physical Properties (Cured @150°C/Tc90+2 Min)
300% Modulus (MPa)	ASTM D412	6.8
Tensile Strength (MPa)	ASTM D412	19.1
Elongation @ Break (%)	ASTM D412	631
Hardness (Shore A)	ASTM D2240	59
Abrasion Properties (Cured @150°C/Tc90+5 Min)
Abrasion Resistance Index (ARI)	ASTM D5963	219
Heat Build Up Properties (Cured @150°C/Tc90+5 Min) - 30Hz, 100°C, 7kg, 25 min
HBU (°C)	ASTM D623	28

PRECURED TREAD- TRUCK & BUS BIAS : PCTR 11

Ingredient	PHR	%
NATURAL RUBBER (RSS 4)	50.00	26.34
CISAMER-01	50.00	26.34
CARBON ISAF-HS N234	60.00	31.61
AROMATIC OIL	17.00	8.95
MC WAX/WAX BLEND	1.00	0.53
ANTIOXIDANT TQ	1.00	0.53
ANTIOXIDANT 6PPD	1.00	0.53
STEARIC ACID	2.00	1.05
ZINC OXIDE	3.00	1.58
CI RESIN	2.00	1.05
RETARDER CTP	0.10	0.05
ACCELERATOR MBS	0.90	0.47
ACCELERATOR TMTD	0.04	0.02
SOLUBLE SULFUR	1.80	0.95
TOTAL	189.84	100.00

Properties	Method	Typical Value
Tc90 @150°C (min)	ASTM D5289	12.4
Physical Properties (Cured @150°C/Tc90+2 Min)
300% Modulus (MPa)	ASTM D412	7.0
Tensile Strength (MPa)	ASTM D412	19.2
Elongation @ Break (%)	ASTM D412	617
Hardness (Shore A)	ASTM D2240	58
Abrasion Properties (Cured @150°C/Tc90+5 Min)
Abrasion Resistance Index (ARI))	ASTM D5963	222
Heat Build Up Properties (Cured @150°C/Tc90+5 Min) - 30Hz, 100°C, 7kg, 25 min
HBU (°C)	ASTM D623	27

PRECURED TREAD- TRUCK & BUS BIAS : PCTR 12

Ingredient	PHR	%
NATURAL RUBBER (RSS 4)	50.00	26.34
CISAMER-700	50.00	26.34
CARBON ISAF-HS N234	60.00	31.61
AROMATIC OIL	17.00	8.96
MC WAX/WAX BLEND	1.00	0.53
ANTIOXIDANT TQ	1.00	0.53
ANTIOXIDANT 6PPD	1.00	0.53
STEARIC ACID	2.00	1.05
ZINC OXIDE	3.00	1.58
CI RESIN	2.00	1.05
RETARDER CTP	0.10	0.05
ACCELERATOR MBS	0.90	0.47
ACCELERATOR TMTD	0.02	0.01
SOLUBLE SULFUR	1.80	0.95
TOTAL	189.82	100.00

Properties	Method	Typical Value
Tc90 @150°C (min)	ASTM D5289	12.7
Physical Properties (Cured @150°C/Tc90+2 Min)
300% Modulus (MPa)	ASTM D412	7.3
Tensile Strength (MPa)	ASTM D412	19.9
Elongation @ Break (%)	ASTM D412	617
Hardness (Shore A)	ASTM D2240	62
Abrasion Properties (Cured @150°C/Tc90+5 Min)
Abrasion Resistance Index (ARI)	ASTM D5963	226
Heat Build Up Properties (Cured @150°C/Tc90+5 Min) - 30Hz, 100°C, 7kg, 25 min
HBU (°C)	ASTM D623	29

PRECURED TREAD- LIGHT DUTY : PCTR 13

Ingredient	PHR	%
NATURAL RUBBER (RSS 4)	35.00	18.07
STYLAMER SBR-1712	34.38	17.74
CISAMER-01	40.00	20.65
CARBON ISAF N220	60.00	30.97
AROMATIC OIL	10.00	5.16
MC WAX/WAX BLEND	1.00	0.52
ANTIOXIDANT TQ	1.00	0.52
ANTIOXIDANT 6PPD	0.50	0.26
STEARIC ACID	2.50	1.29
ZINC OXIDE	4.00	2.06
PF RESIN	2.00	1.03
ACCELERATOR MBS	1.20	0.62
ACCELERATOR TMTD	0.15	0.08
SOLUBLE SULFUR	2.00	1.03
TOTAL	193.73	100.00

Properties	Method	Typical Value
Tc90 @150°C (min)	ASTM D5289	10.9
Physical Properties (Cured @150°C/Tc90+2 Min)
300% Modulus (MPa)	ASTM D412	8.4
Tensile Strength (MPa)	ASTM D412	19.6
Elongation @ Break (%)	ASTM D412	541
Hardness (Shore A)	ASTM D2240	61
Abrasion Properties (Cured @150°C/Tc90+5 Min)
Abrasion Resistance Index (ARI)	ASTM D5963	189

PRECURED TREAD -MEDIUM DUTY - PCTR 14

Ingredient	PHR	%
ISNR 20	25.00	13.59
STYLAMER SBR-1502	25.00	13.59
CISAMER-01	50.00	27.19
HOMOGENISER	2.00	1.09
CARBON ISAF HS N234	55.00	29.91
PROCESS OIL	13.00	7.07
MC WAX	1.00	0.54
ANTIOXIDANT TQ	1.00	0.54
ANTIOXIDANT 6PPD	1.50	0.82
STEARIC ACID	2.00	1.09
ZINC OXIDE	3.50	1.90
PF RESIN	2.00	1.09
ACCELERATOR TBBS	1.00	0.54
SOLUBLE SULFUR	1.90	1.03
TOTAL	183.90	100.00

Properties	Method	Typical Value
Tc90 @150°C (min)	ASTM D5289	13.0
Physical Properties (Cured @150°C/Tc90+2 Min)
300% Modulus (MPa)	ASTM D412	8.2
Tensile Strength (MPa)	ASTM D412	20.0
Elongation @ Break (%)	ASTM D412	615
Hardness (Shore A)	ASTM D2240	62
Abrasion Properties (Cured @150°C/Tc90+5 Min)
Abrasion Resistance Index (ARI)	ASTM D5963	220

PRECURED TREAD- LIGHT DUTY : PCTR 15

Ingredient	PHR	%
ISNR 20	30.00	15.45
STYLAMER SBR-1712	34.38	17.70
CISAMER-01	45.00	23.17
CARBON ISAF N234	60.00	30.89
AROMATIC OIL	10.00	5.15
MC WAX	1.00	0.51
ANTIOXIDANT TQ	1.00	0.51
ANTIOXIDANT 6PPD	1.50	0.77
STEARIC ACID	2.50	1.29
ZINC OXIDE	4.00	2.06
PF RESIN	1.50	0.77
ACCELERATOR MBS	1.20	0.62
ACCELERATOR TMTD	0.15	0.08
SOLUBLE SULFUR	2.00	1.03
TOTAL	194.23	100.00

Properties	Method	Typical Value
Tc90 @150°C (min)	ASTM D5289	13.0
Physical Properties (Cured @150°C/Tc90+2 Min)
300% Modulus (MPa)	ASTM D412	9.5
Tensile Strength (MPa)	ASTM D412	19.0
Elongation @ Break (%)	ASTM D412	520
Hardness (Shore A)	ASTM D2240	62
Abrasion Properties (Cured @150°C/Tc90+5 Min)
Abrasion Resistance Index (ARI)	ASTM D5963	190

SOLID TYRE TREAD : STANDARD

Ingredient	PHR	%
NATURAL RUBBER (RSS 4)	50.00	27.75
CISAMER-01	10.00	5.55
STYLAMER SBR-1502	40.00	22.20
CARBON HAF N330	55.00	30.52
AROMATIC OIL	10.00	5.55
MC WAX/WAX BLEND	1.00	0.55
ANTIOXIDANT 6PPD	1.50	0.83
ANTIOXIDANT TMQ	1.50	0.83
PF RESIN (1811)	1.00	0.55
PROCESSING AID A73	1.00	0.55
PEPTIZER DBD	0.10	0.06
STEARIC ACID	2.00	1.11
ZINC OXIDE	4.00	2.22
ACCELERATOR TMTD	0.20	0.11
ACCELERATOR TBBS	1.30	0.72
SULFUR	1.60	0.89
TOTAL	180.20	100.00

Properties	Method	Typical Value
Tc90 @145°C (min)	ASTM D5289	12.2
Physical Properties (Cured @145°C/Tc90+2 Min)
300% Modulus (MPa)	ASTM D412	13.1
Tensile Strength (MPa)	ASTM D412	21.2
Elongation @ Break (%)	ASTM D412	447
Hardness (Shore A)	ASTM D2240	65
Abrasion Properties (Cured @145°C/Tc90+5 Min)
Abrasion Loss (mm³)	ASTM D5963	122
Heat Build Up Properties (Cured @145°C/Tc90+5 Min) - 30Hz, 100°C, 7 kg, 25 min
HBU (°C)	ASTM D623	14

SOLID TYRE TREAD : LOW ROLLING RESISTANCE

Ingredient	PHR	%
NATURAL RUBBER (RSS 4)	60.00	32.17
CISAMER-01	40.00	21.45
PPT SILICA VN3	55.00	29.49
SILANE COUPLING AGENT Si-69	5.00	2.68
PEG 4000	2.00	1.07
AROMATIC OIL	8.00	4.29
ANTIOXIDANT TDQ	1.50	0.80
STEARIC ACID	1.00	0.54
ZINC OXIDE	5.00	2.68
TITANIUM DIOXIDE	3.50	1.88
ACCELERATOR CBS	1.50	0.80
SULFUR	2.50	1.34
ACCELERATOR DPG	1.50	0.80
TOTAL	186.50	100.00

Properties	Method	Typical Value
Tc90 @160°C (min)	ASTM D5289	2.6
Physical Properties (Cured @160°C/Tc90+1 Min)
300% Modulus (MPa)	ASTM D412	13.9
Tensile Strength (MPa)	ASTM D412	18.4
Elongation @ Break (%)	ASTM D412	386
Hardness (Shore A)	ASTM D2240	66
Tear Strength (Kgs/mm)	ASTM D624	8.5
Dynamic Properties Properties (Cured @160°C/Tc90+1 Min) - 2% Static Strain, 1% Dynamic Strain, 1Hz - Tension Mode
tan δ @60°C	ASTM D5992	0.08

Rice Polisher Brake : RPB 1

Ingredient	PHR	%
NATURAL RUBBER (RSS 4)	40.00	10.91
STYLAMER SBR-1502	30.00	8.19
CISAMER-01	30.00	8.19
PEPTISER DBD	0.10	0.03
CHINA CLAY	210.00	57.30
SPINDLE OIL	35.00	9.55
TACKIFYING RESIN	1.50	0.41
TITANIUM DIOXIDE	1.30	0.35
DIETHYLENE GLYCOL	1.00	0.27
ANTIOXIDANT SP	1.30	0.35
STEARIC ACID	2.50	0.68
ZINC OXIDE	9.00	2.46
ACCELERATOR CBS	1.70	0.46
ACCELERATOR TMT	0.30	0.08
SULFUR	2.80	0.76
TOTAL	366.50	100.00

Properties	Method	Typical Value
Tc90 @140°C (min)	ASTM D5289	22.0
Physical Properties (Cured @140°C/Tc90+2 min)
300% Modulus (MPa)	ASTM D412	4.1
Tensile Strength (MPa)	ASTM D412	6.7
Elongation @ Break (%)	ASTM D412	517
Hardness (Shore A)	ASTM D2240	61
Abrasion Properties (Cured @140°C/Tc90+5 Min)
Abrasion Loss (mm³)	ASTM D5963	399

Rice Polisher Brake : RPB 2

Ingredient	PHR	%
NATURAL RUBBER (RSS 4)	40.00	15.62
STYLAMER SBR-1502	30.00	11.71
CISAMER-01	30.00	11.71
PEPTISER DBD	0.10	0.04
PPT SILICA VN3	11.00	4.29
CHINA CLAY	90.00	35.14
ALUMINIUM SILICATE	14.00	5.47
SPINDLE OIL	20.00	7.81
TACKIFYING RESIN	1.50	0.59
TITANIUM DIOXIDE	1.30	0.51
DIETHYLENE GLYCOL	1.00	0.39
ANTIOXIDANT SP	1.30	0.51
STEARIC ACID	2.50	0.98
ZINC OXIDE	9.00	3.51
ACCELERATOR CBS	1.50	0.59
ACCELERATOR TMT	0.15	0.06
SULFUR	2.80	1.09
TOTAL	256.15	100.00

Properties	Method	Typical Value
Tc90 @140°C (min)	ASTM D5289	17.0
Physical Properties (Cured @140°C/Tc90+2 min)
300% Modulus (MPa)	ASTM D412	4.4
Tensile Strength (MPa)	ASTM D412	8.3
Elongation @ Break (%)	ASTM D412	471
Hardness (Shore A)	ASTM D2240	64
Abrasion Properties (Cured @140°C/Tc90+5 Min)
Abrasion Loss (mm³)	ASTM D5963	296

Rubber Shoe Sole - Moulded : SS 1

Ingredient	PHR	%
NATURAL RUBBER (RSS 4)	20.00	11.06
STYLAMER SBR-1502	30.00	16.59
CISAMER-01	50.00	27.65
PPT SILICA VN3	40.00	22.12
CARBON HAF N330	15.00	8.29
SILANE COUPLING AGENT Si-69	0.40	0.22
AROMATIC OIL	12.00	6.64
PEG 4000	3.00	1.66
ANTIOXIDANT TMQ	0.75	0.41
STEARIC ACID	1.00	0.55
ZINC OXIDE	4.50	2.49
ACCELERATOR MBTS	1.00	0.55
ACCELERATOR MBT	1.00	0.55
ACCELERATOR TMTD	0.20	0.11
SULFUR	2.00	1.11
TOTAL	180.85	100.00

Properties	Method	Typical Value
Tc90 @165°C (min)	ASTM D5289	3.0
Physical Properties (Cured @165°C/Tc90+2 min)
100% Modulus (MPa)	ASTM D412	4.3
Tensile Strength (MPa)	ASTM D412	12.2
Elongation @ Break (%)	ASTM D412	271
Hardness (Shore A)	ASTM D2240	70
Abrasion Properties (Cured @ 165°C/Tc90+5 min)
Abrasion Loss (mm³)	ASTM D5963	83

RUBBER SHOE SOLE - Moulded : SS 2

Ingredient	PHR	%
NATURAL RUBBER (RSS 4)	20.00	11.86
CISAMER-01	40.00	23.72
STYLAMER SBR-1502	40.00	23.72
PPT SILICA VN3	40.00	23.72
CARBON GPF N660	6.00	3.56
SILANE COUPLING AGENT Si-69	2.00	1.19
NAPTHENIC OIL	3.00	1.78
HOMOGENISER	1.50	0.89
POLYETHYLENE GLYCOL	4.00	2.37
ANTIOXIDANT TQ	2.00	1.19
STEARIC ACID	1.00	0.59
ZINC OXIDE	5.00	2.96
ACCELERATOR DPG	0.30	0.18
ACCELERATOR MBTS	1.05	0.62
ACCELERATOR TBzTD	0.30	0.18
INSOLUBLE SULFUR	2.50	1.48
TOTAL	168.65	100.00

Properties	Method	Typical Value
Tc90 @155°C (min)	ASTM D5289	5.0
Physical Properties (Cured @155°C/Tc90+2 Min)
300% Modulus (MPa)	ASTM D412	9.5
Tensile Strength (MPa)	ASTM D412	17.1
Elongation @ Break (%)	ASTM D412	481
Hardness (Shore A)	ASTM D2240	63
Abrasion Properties (Cured @155°C/Tc90+5 Min)
Abrasion Loss (mm³)	ASTM D5963	83

RUBBER SHOE SOLE - Moulded : SS 3

Ingredient	PHR	%
NATURAL RUBBER (RSS 4)	25.00	14.29
CISAMER-01	50.00	28.57
STYLAMER SBR-1502	25.00	14.29
PPT SILICA VN3	45.00	25.71
CARBON GPF N660	6.00	3.43
SILANE COUPLING AGENT Si-69	2.50	1.43
NAPTHENIC OIL	4.00	2.29
HOMOGENISER	1.50	0.86
POLYETHYLENE GLYCOL	4.00	2.29
ANTIOXIDANT TQ	2.00	1.14
STEARIC ACID	1.00	0.57
ZINC OXIDE	5.00	2.86
ACCELERATOR DPG	0.20	0.11
ACCELERATOR MBTS	0.90	0.51
ACCELERATOR TBzTD	0.20	0.11
INSOLUBLE SULFUR	2.70	1.54
TOTAL	175.00	100.00

Properties	Method	Typical Value
Tc90 @155°C (min)	ASTM D5289	5.6
Physical Properties (Cured @155°C/Tc90+2 Min)
300% Modulus (MPa)	ASTM D412	8.6
Tensile Strength (MPa)	ASTM D412	18.1
Elongation @ Break (%)	ASTM D412	550
Hardness (Shore A)	ASTM D2240	61
Abrasion Properties (Cured @155°C/Tc90+5 Min)
Abrasion Loss (mm³)	ASTM D5963	70

RUBBER SHOE SOLE - Moulded : SS 4

Ingredient	PHR	%
NATURAL RUBBER (RSS 4)	50.00	30.04
CISAMER-01	50.00	30.04
PPT SILICA VN3	40.00	24.03
CARBON GPF N660	6.00	3.60
SILANE COUPLING AGENT Si-69	2.00	1.20
NAPTHENIC OIL	3.00	1.80
POLYETHYLENE GLYCOL	3.70	2.22
ANTIOXIDANT TQ	2.00	1.20
STEARIC ACIDL	1.00	0.60
ZINC OXIDE	5.00	3.00
ACCELERATOR MBTS	1.10	0.66
ACCELERATOR TBzTD	0.35	0.21
INSOLUBLE SULFUR	2.30	1.38
TOTAL	166.45	100.00

Properties	Method	Typical Value
Tc90 @155°C (min)	ASTM D5289	4.2
Physical Properties (Cured @155°C/Tc90+2 Min)
300% Modulus (MPa)	ASTM D412	7.3
Tensile Strength (MPa)	ASTM D412	20.5
Elongation @ Break (%)	ASTM D412	641
Hardness (Shore A)	ASTM D2240	61
Abrasion Properties (Cured @155°C/Tc90+5 Min)
Abrasion Loss (mm³)	ASTM D5963	77

Pharma Stoppers- Bromobutyl : PS 1

Ingredient	PHR	%
BROMOBUTYL IMPRAMER B2232	100.00	55.25
CALCINED CLAY	70.00	38.67
TITANIUM DIOXIDE	2.00	1.10
POLYETHYLENE	5.00	2.76
COLOUR PIGMENT	1.00	0.55
ACCELERATOR ZDEC	0.50	0.28
ZINC OXIDE	2.50	1.38
TOTAL	181.00	100.00

Properties	Method	Typical Value
Tc90 @160°C (Min)	ASTM D5289	18.0
Physical Properties (Cured @160°C/Tc90+3 Min)
300% Modulus (MPa)	ASTM D412	3.2
Tensile Strength (MPa)	ASTM D412	7.5
Elongation @ Break (%)	ASTM D412	700
Hardness (Shore A)	ASTM D2240	45

PHARMA STOPPERS- BROMOBUTYL : PS 2

Ingredient	PHR	%
BROMOBUTYL IMPRAMER B2232	100.00	57.64
PPT SILICA VN3	5.00	2.88
CLACINED CLAY	55.00	31.70
TITANIUM DIOXIDE	2.00	1.15
MAGNESIUM OXIDE	0.25	0.14
STEARIC ACID	1.00	0.58
LOW DENSITY POLYETHYLENE	5.00	2.88
ZINC OXIDE	3.00	1.73
ACCELERATOR TBzTD	1.50	0.86
SOLUBLE SULFUR	0.75	0.43
TOTAL	173.50	100.00

Properties	Method	Typical Value
Tc90 @175°C (min)	ASTM D5289	5.8
Physical Properties (Cured @175°C/Tc90+2 Min)
300% Modulus (MPa)	ASTM D412	1.4
Tensile Strength (MPa)	ASTM D412	7.6
Elongation @ Break (%)	ASTM D412	962
Hardness (Shore A)	ASTM D2240	36

PHARMA STOPPERS- BROMOBUTYL : PS 3

Ingredient	PHR	%
BROMOBUTYL IMPRAMER B2232	100.00	56.74
PPT SILICA VN3	5.00	2.84
CLACINED CLAY	55.00	31.21
TITANIUM DIOXIDE	2.00	1.13
MAGNESIUM OXIDE	0.25	0.14
STEARIC ACID	1.00	0.57
LOW DENSITY POLYETHYLENE	5.00	2.84
ZINC OXIDE	3.00	1.70
BROMINATED CURING RESIN	5.00	2.84
TOTAL	176.25	100.00

Properties	Method	Typical Value
Tc90 @175°C (min)	ASTM D5289	10.7
Physical Properties (Cured @175°C/Tc90+2 Min)
300% Modulus (MPa)	ASTM D412	1.7
Tensile Strength (MPa)	ASTM D412	6.5
Elongation @ Break (%)	ASTM D412	845
Hardness (Shore A)	ASTM D2240	40

PHARMA STOPPERS- BROMOBUTYL : PS 4

Ingredient	PHR	%
BROMOBUTYL IMPRAMER B2232	100.00	56.74
PPT SILICA VN3	5.00	2.84
CLACINED CLAY	55.00	31.21
TITANIUM DIOXIDE	2.00	1.13
STEARIC ACID	1.00	0.14
LOW DENSITY POLYETHYLENE	5.00	0.57
MAGNESIUM OXIDE	3.00	1.70
HEXAMETHYLENEDIAMINE CARBAMATE	1.00	2.84
TOTAL	172.00	100.00

Properties	Method	Typical Value
Tc90 @175°C (min)	ASTM D5289	6.6
Physical Properties (Cured @175°C/Tc90+2 Min)
300% Modulus (MPa)	ASTM D412	2.0
Tensile Strength (MPa)	ASTM D412	5.8
Elongation @ Break (%)	ASTM D412	705
Hardness (Shore A)	ASTM D2240	42

MOULDED RUBBER PRODUCT - 40 HARDNESS : MRP 40

Ingredient	PHR	%
NATURAL RUBBER (RSS 4)	60.00	22.73
STYLAMER SBR-1502	40.00	15.15
CARBON HAF N330	10.00	3.79
CHINA CLAY	100.00	37.88
AROMATIC OIL	40.00	15.15
ZINC OXIDE	5.00	1.89
STEARIC ACID	1.50	0.57
ANTIOXIDANT TMQ	1.00	0.38
ANTIOXIDANT 6PPD	0.50	0.19
CI RESIN	2.00	0.76
PARAFFINIC WAX	1.00	0.38
ACCELERATOR MBTS	1.40	0.53
ACCELERATOR TMT	0.20	0.08
SULFUR	1.40	0.53
TOTAL	264.00	100.00

Properties	Method	Typical Value
Tc90 @160°C (min)	ASTM D5289	4.3
Physical Properties (Cured @160°C/Tc90+2 Min)
300% Modulus (MPa)	ASTM D412	2.9
Tensile Strength (MPa)	ASTM D412	8.8
Elongation @ Break (%)	ASTM D412	612
Hardness (Shore A)	ASTM D2240	40

MOULDED RUBBER PRODUCT - 50 HARDNESS : MRP 50

Ingredient	PHR	%
NATURAL RUBBER (RSS 4)	50.00	19.29
STYLAMER SBR-1502	50.00	19.29
CARBON HAF N330	20.00	7.72
CHINA CLAY	100.00	38.58
AROMATIC OIL	25.00	9.65
ZINC OXIDE	5.00	1.93
STEARIC ACID	1.50	0.58
ANTIOXIDANT TMQ	1.00	0.39
ANTIOXIDANT 6PPD	0.50	0.19
CI RESIN	2.00	0.77
PARAFFINIC WAX	1.00	0.39
ACCELERATOR MBTS	1.30	0.50
ACCELERATOR TMT	0.20	0.08
SULFUR	1.70	0.66
TOTAL	259.20	100.00

Properties	Method	Typical Value
Tc90 @160°C (min)	ASTM D5289	6.8
Physical Properties (Cured @160°C/Tc90+2 Min)
300% Modulus (MPa)	ASTM D412	4.4
Tensile Strength (MPa)	ASTM D412	11.6
Elongation @ Break (%)	ASTM D412	597
Hardness (Shore A)	ASTM D2240	52

MOULDED RUBBER PRODUCT - 60 HARDNESS : MRP 60

Ingredient	PHR	%
NATURAL RUBBER (RSS 4)	50.00	18.91
STYLAMER SBR-1502	50.00	18.91
CARBON HAF N330	30.00	11.35
CHINA CLAY	100.00	37.82
AROMATIC OIL	20.00	7.56
ZINC OXIDE	5.00	1.89
STEARIC ACID	1.50	0.57
ANTIOXIDANT TMQ	1.00	0.38
ANTIOXIDANT 6PPD	0.50	0.19
CI RESIN	2.00	0.76
PARAFFINIC WAX	1.00	0.38
ACCELERATOR MBTS	1.30	0.49
ACCELERATOR TMT	0.20	0.08
SULFUR	1.90	0.72
TOTAL	264.40	100.00

Properties	Method	Typical Value
Tc90 @160°C (min)	ASTM D5289	5.6
Physical Properties (Cured @160°C/Tc90+2 Min)
300% Modulus (MPa)	ASTM D412	6.3
Tensile Strength (MPa)	ASTM D412	13.6
Elongation @ Break (%)	ASTM D412	563
Hardness (Shore A)	ASTM D2240	62

MOULDED RUBBER PRODUCT - 70 HARDNESS : MRP 70

Ingredient	PHR	%
NATURAL RUBBER (RSS 4)	50.00	18.55
STYLAMER SBR-1502	50.00	18.55
CARBON HAF N330	40.00	14.84
CHINA CLAY	100.00	37.09
AROMATIC OIL	15.00	5.56
ZINC OXIDE	5.00	1.85
STEARIC ACID	1.50	0.56
ANTIOXIDANT TMQ	1.00	0.37
ANTIOXIDANT 6PPD	0.50	0.19
CI RESIN	2.00	0.74
PARAFFINIC WAX	1.00	0.37
ACCELERATOR MBTS	1.30	0.48
ACCELERATOR TMT	0.20	0.07
SULFUR	2.10	0.78
TOTAL	269.60	100.00

Properties	Method	Typical Value
Tc90 @160°C (min)	ASTM D5289	4.2
Physical Properties (Cured @160°C/Tc90+2 Min)
300% Modulus (MPa)	ASTM D412	10.3
Tensile Strength (MPa)	ASTM D412	16.1
Elongation @ Break (%)	ASTM D412	485
Hardness (Shore A)	ASTM D2240	73

MOULDED RUBBER PRODUCT - 80 HARDNESS : MRP 80

Ingredient	PHR	%
NATURAL RUBBER (RSS 4)	50.00	18.20
STYLAMER SBR-1502	50.00	18.20
CARBON HAF N330	50.00	18.20
CHINA CLAY	100.00	36.39
AROMATIC OIL	10.00	3.64
ZINC OXIDE	5.00	1.82
STEARIC ACID	1.50	0.55
ANTIOXIDANT TMQ	1.00	0.36
ANTIOXIDANT 6PPD	0.50	0.18
CI RESIN	2.00	0.73
PARAFFINIC WAX	1.00	0.36
ACCELERATOR MBTS	1.30	0.47
ACCELERATOR TMT	0.20	0.07
SULFUR	2.30	0.84
TOTAL	274.80	100.00

Properties	Method	Typical Value
Tc90 @160°C (min)	ASTM D5289	3.5
Physical Properties (Cured @160°C/Tc90+2 Min)
300% Modulus (MPa)	ASTM D412	12.7
Tensile Strength (MPa)	ASTM D412	16.0
Elongation @ Break (%)	ASTM D412	408
Hardness (Shore A)	ASTM D2240	79

MOULDED RUBBER PRODUCT - 90 HARDNESS : MRP 90

Ingredient	PHR	%
NATURAL RUBBER (RSS 4)	50.00	17.24
STYLAMER SBR-1502	50.00	17.24
CARBON HAF N330	70.00	24.13
CHINA CLAY	100.00	34.48
AROMATIC OIL	5.00	1.72
ZINC OXIDE	5.00	1.72
STEARIC ACID	1.50	0.52
ANTIOXIDANT TMQ	1.00	0.34
ANTIOXIDANT 6PPD	0.50	0.17
CI RESIN	2.00	0.69
PARAFFINIC WAX	1.00	0.34
ACCELERATOR MBTS	1.00	0.45
ACCELERATOR TMT	0.15	0.05
SOLUBLE SULFUR	2.60	0.90
TOTAL	290.05	100.00

Properties	Method	Typical Value
Tc90 @160°C (min)	ASTM D5289	4.5
Physical Properties (Cured @160°C/Tc90+2 Min)
300% Modulus (MPa)	ASTM D412	NIL
Tensile Strength (MPa)	ASTM D412	15.4
Elongation @ Break (%)	ASTM D412	282
Hardness (Shore A)	ASTM D2240	87

MOULDED RUBBER PRODUCT (NON-BLACK)- 40 HARDNESS : MRP S40

Ingredient	PHR	%
NATURAL RUBBER (RSS 4)	60.00	22.97
STYLAMER SBR-1502	40.00	15.31
PPT SILICA VN3	10.00	3.83
CHINA CLAY	100.00	38.28
NAPHTHENIC OIL	38.00	14.55
DIETHYLENE GLYCOL	0.75	0.29
PARAFFINIC WAX	1.00	0.38
STEARIC ACID	1.50	0.57
ZINC OXIDE	5.00	1.91
CI RESIN	2.00	0.77
ACCELERATOR MBTS	1.40	0.54
ACCELERATOR TMT	0.20	0.08
SOLUBLE SULFUR	1.40	0.54
TOTAL	261.25	100.00

Properties	Method	Typical Value
Tc90 @160°C (min)	ASTM D5289	5.9
Physical Properties (Cured @160°C/Tc90+2 Min)
300% Modulus (MPa)	ASTM D412	3.0
Tensile Strength (MPa)	ASTM D412	11.5
Elongation @ Break (%)	ASTM D412	730
Hardness (Shore A)	ASTM D2240	40

MOULDED RUBBER PRODUCT(NON-BLACK) - 50 HARDNESS : MRP S50

Ingredient	PHR	%
NATURAL RUBBER (RSS 4)	50.00	19.40
STYLAMER SBR-1502	50.00	19.40
PPT SILICA VN3	20.00	7.76
CHINA CLAY	100.00	38.80
NAPHTHENIC OIL	24.00	9.31
DIETHYLENE GLYCOL	1.00	0.39
PARAFFINIC WAX	1.00	0.39
STEARIC ACID	1.50	0.58
ZINC OXIDE	5.00	1.94
CI RESIN	2.00	0.78
ACCELERATOR MBTS	1.30	0.50
ACCELERATOR TMT	0.20	0.08
SOLUBLE SULFUR	1.70	0.66
TOTAL	257.70	100.00

Properties	Method	Typical Value
Tc90 @160°C (min)	ASTM D5289	7.3
Physical Properties (Cured @160°C/Tc90+2 Min)
300% Modulus (MPa)	ASTM D412	3.4
Tensile Strength (MPa)	ASTM D412	12.1
Elongation @ Break (%)	ASTM D412	679
Hardness (Shore A)	ASTM D2240	49

MOULDED RUBBER PRODUCT(NON-BLACK) - 60 HARDNESS : MRP S60

Ingredient	PHR	%
NATURAL RUBBER (RSS 4)	50.00	19.01
STYLAMER SBR-1502	50.00	19.01
PPT SILICA VN3	30.00	11.41
CHINA CLAY	100.00	38.02
NAPHTHENIC OIL	18.50	7.03
DIETHYLENE GLYCOL	1.50	0.57
PARAFFINIC WAX	1.00	0.38
STEARIC ACID	1.50	0.57
ZINC OXIDE	5.00	1.90
CI RESIN	2.00	0.76
ACCELERATOR MBTS	1.35	0.51
ACCELERATOR TMT	0.25	0.10
SOLUBLE SULFUR	1.90	0.72
TOTAL	263.00	100.00

Properties	Method	Typical Value
Tc90 @160°C (min)	ASTM D5289	5.8
Physical Properties (Cured @160°C/Tc90+2 Min)
300% Modulus (MPa)	ASTM D412	4.2
Tensile Strength (MPa)	ASTM D412	13.4
Elongation @ Break (%)	ASTM D412	675
Hardness (Shore A)	ASTM D2240	57

MOULDED RUBBER PRODUCT(NON-BLACK) - 70 HARDNESS : MRP S70

Ingredient	PHR	%
NATURAL RUBBER (RSS 4)	50.00	18.64
STYLAMER SBR-1502	50.00	18.64
PPT SILICA VN3	40.00	14.91
CHINA CLAY	100.00	37.29
NAPHTHENIC OIL	13.50	4.85
DIETHYLENE GLYCOL	2.00	0.75
PARAFFINIC WAX	1.00	0.37
STEARIC ACID	1.50	0.56
ZINC OXIDE	5.00	1.86
CI RESIN	2.00	0.75
ACCELERATOR MBTS	1.35	0.50
ACCELERATOR TMT	0.25	0.09
SOLUBLE SULFUR	2.10	0.78
TOTAL	268.20	100.00

Properties	Method	Typical Value
Tc90 @160°C (min)	ASTM D5289	5.0
Physical Properties (Cured @160°C/Tc90+2 Min)
300% Modulus (MPa)	ASTM D412	5.1
Tensile Strength (MPa)	ASTM D412	14.7
Elongation @ Break (%)	ASTM D412	649
Hardness (Shore A)	ASTM D2240	69

MOULDED RUBBER PRODUCT(NON-BLACK) - 80 HARDNESS : MRP S80

Ingredient	PHR	%
NATURAL RUBBER (RSS 4)	50.00	18.28
STYLAMER SBR-1502	50.00	18.28
PPT SILICA VN3	50.00	18.28
CHINA CLAY	100.00	36.56
NAPHTHENIC OIL	7.00	2.56
DIETHYLENE GLYCOL	3.00	1.10
PARAFFINIC WAX	1.00	0.37
STEARIC ACID	1.50	0.55
ZINC OXIDE	5.00	1.83
CI RESIN	2.00	0.73
ACCELERATOR MBTS	1.40	0.51
ACCELERATOR TMT	0.30	0.11
SOLUBLE SULFUR	2.30	0.84
TOTAL	273.50	100.00

Properties	Method	Typical Value
Tc90 @160°C (min)	ASTM D5289	5.1
Physical Properties (Cured @160°C/Tc90+2 Min)
300% Modulus (MPa)	ASTM D412	6.4
Tensile Strength (MPa)	ASTM D412	16
Elongation @ Break (%)	ASTM D412	603
Hardness (Shore A)	ASTM D2240	78

MOULDED RUBBER PRODUCT(NON-BLACK) - 90 HARDNESS : MRP S90

Ingredient	PHR	%
NATURAL RUBBER (RSS 4)	50.00	17.31
STYLAMER SBR-1502	50.00	17.31
PPT SILICA VN3	70.00	24.24
CHINA CLAY	100.00	34.63
NAPHTHENIC OIL	1.00	0.35
DIETHYLENE GLYCOL	4.00	1.39
PARAFFINIC WAX	1.00	0.35
STEARIC ACID	1.50	0.52
ZINC OXIDE	5.00	1.73
CI RESIN	2.00	0.69
ACCELERATOR MBTS	1.40	0.48
ACCELERATOR TMT	0.30	0.10
SOLUBLE SULFUR	2.60	0.90
TOTAL	288.80	100.00

Properties	Method	Typical Value
Tc90 @160°C (min)	ASTM D5289	6.0
Physical Properties (Cured @160°C/Tc90+2 Min)
300% Modulus (MPa)	ASTM D412	8.8
Tensile Strength (MPa)	ASTM D412	14
Elongation @ Break (%)	ASTM D412	598
Hardness (Shore A)	ASTM D2240	91

GENERAL PURPOSE WATER PROOFING RUBBER LININIG

Ingredient	PHR	%
EPDM RUBBER (LOW ENB/40 MOONEY)	30.00	13.30
BUTYL IMPRAMER R 1675	70.00	31.04
CARBON FEF 550	55.00	24.39
PRECIPITED SILICA	10.00	4.43
STEARIC ACID	1.00	0.44
PEG4000	5.00	2.22
PE WAX	5.00	2.22
CALCINED CLAY	30.00	13.30
NAPTHENIC OIL	10.00	4.43
ZINC OXIDE (FINAL)	4.00	1.77
ACCELERATOR TMTD	1.50	0.67
ACCELERATOR ZDBC	0.50	0.22
ACCELERATOR MBTS	1.00	0.44
SULFUR	1.50	0.67
ANTIOXIDANT DPPD	1.00	0.44
TOTAL	225.50	100.00

Properties	Method	Typical Value
Tc90 @160°C (min)	ASTM D5289	16
Physical Properties (Cured @160°C/Tc90+2 Min)
300% Modulus (MPa)	ASTM D412	6.8
Tensile Strength (MPa)	ASTM D412	10.0
Elongation @ Break (%)	ASTM D412	450
Tension Set (%) @ 50%Stretch	ASTM D412	6.0
Hardness (Shore A)	ASTM D2240	62

PHARMA STOPPER-CIIR-1

Ingredient	PHR	%
CHLOROBUTYL RUBBER IMPRAMER C1139	100.00	57.74
CALCINED CLAY	60.00	34.64
LOW DENSITY POLYETHENE	5.0	2.89
TiO2	2.0	1.15
STEARIC ACID	2.00	1.15
MAGNESIUM OXIDE	0.2	0.12
ZINC OXIDE (FINAL)	2.50	1.44
ACCELERATOR ZBzDC	0.50	0.29
VULTAC 5	1.00	0.58
TOTAL	173.20	100.00

Properties	Method	Typical Value
Tc90 @160°C (min)	ASTM D5289	6
Physical Properties (Cured @160°C/Tc90+2 Min)
300% Modulus (MPa)	ASTM D412	3.0
Tensile Strength (MPa)	ASTM D412	7.5
Elongation @ Break (%)	ASTM D412	900
Hardness (Shore A)	ASTM D2240	45

PHARMA STOPPER-CIIR-2

Ingredient	PHR	%
CHLOROBUTYL RUBBER IMPRAMER C1139	100.00	57.80
CALCINED CLAY	60.00	34.68
LOW DENSITY POLYETHENE	5.0	2.89
TiO2	2.0	1.16
STEARIC ACID	2.0	1.16
ZINC OXIDE (FINAL)	2.50	1.45
ACCELERATOR MBTS	0.50	0.29
ACCELERATOR TMTD	0.50	0.29
SULFUR	0.50	0.29
TOTAL	173.00	100.00

Properties	Method	Typical Value
Tc90 @160°C (min)	ASTM D5289	5.0
Physical Properties (Cured @160°C/Tc90+2 Min)
300% Modulus (MPa)	ASTM D412	1.7
Tensile Strength (MPa)	ASTM D412	7.6
Elongation @ Break (%)	ASTM D412	950
Hardness (Shore A)	ASTM D2240	42

PHARMA STOPPER-IIR

Ingredient	PHR	%
BUTYL RUBBER IMPRAMER R 1675	100.00	55.68
CALCINED CLAY	65.0	36.19
LOW DENSITY POLYETHENE	3.0	1.67
PEG4000	1.5	0.84
TiO2	3.0	1.67
STEARIC ACID	1.0	0.56
ZINC OXIDE (FINAL)	3.00	1.67
ACCELERATOR MBTS	0.50	0.28
ACCELERATOR TMTD	1.00	0.56
ACCELERATOR ZDBC	0.50	0.28
SULFUR	1.10	0.61
TOTAL	179.60	100.00

Properties	Method	Typical Value
Tc90 @160°C (min)	ASTM D5289	15.0
Physical Properties (Cured @160°C/Tc90+2 Min)
300% Modulus (MPa)	ASTM D412	1.9
Tensile Strength (MPa)	ASTM D412	5.0
Elongation @ Break (%)	ASTM D412	600
Hardness (Shore A)	ASTM D2240	46

BUTYL BASED TYRE FLAP

Ingredient	PHR	%
BUTYL RUBBER IMPRAMER R 1675	65	28.60
EPDM RUBBER (LOW ENB/40 MOONEY)	15	6.60
BUTYL RECLAIM RUBBER	40	17.60
CARBON GPF N660	65	28.60
CARBON HAF N330	15	6.60
PARRAFINIC OIL	18	7.92
ZINC OXIDE	3	1.32
STEARIC ACID	2	0.88
SULFUR	1.5	0.66
ACCELERATOR MBT	0.5	0.22
ACCELERATOR TMT	1.5	0.66
ACCELERATOR ZDEC	0.75	0.33
TOTAL	227.25	100.00

Properties	Method	Typical Value
Tc90 @160°C (min)	ASTM D5289	15.0
Physical Properties (Cured @160°C/Tc90+2 Min)
300% Modulus (MPa)	ASTM D412	7.5
Tensile Strength (MPa)	ASTM D412	9.5
Elongation @ Break (%)	ASTM D412	430
Hardness (Shore A)	ASTM D2240	60

MILL LINER

Ingredient	PHR	%
NATURAL RUBBER (RMA/RSS IV)	50	28.4
POLYBUTADIENE RUBBER CISA 01 HMD	50	28.4
CARBON BLACK N330 ( HAF )	50	28.4
PROCESS OIL 710	10	5.7
ZINC OXIDE	4.0	2.3
STEARIC ACID	2.0	1.1
M.C. WAX	2.0	1.1
ANTIOXIDANT 6 PPD	1.0	0.6
ANTIOXIDANT TQ	1.0	0.6
PF RESIN	2.5	1.4
ACCELERATOR CBS	1.5	0.9
SULFUR	2.0	1.1
TOTAL	176.0	100.0

Properties	Method	Typical Value
Tc90 @150°C/30 min	ASTM D5289	9.0
Physical Properties (Cured @ 150°C/ Tc90+2 min)
300% Modulus (MPa)	ASTM D412	7.6
Tensile Strength (MPa)	ASTM D412	21.2
Elongation @ Break (%)	ASTM D412	587
Hardness (Shore A)	ASTM D2240	61
Abrasion Properties (Cured at 150°C/ Tc90+5 min)
Abrasion Loss (mm³)	ASTM D5963	52.0

BUTYL/CHLOROBUTYL TUBE

Ingredient	PHR	%
BUTYL IMPRAMER R 1675	90.00	44.01
CHLOROBUTYL RUBBER IMPRAMER C1139	10.00	4.89
CARBON GPF N660	70.0	34.23
PARAFFINIC OIL	25.0	12.22
ZINC OXIDE	5.0	2.44
STEARIC ACID	1.0	0.49
ACCELERATOR TMTD	1.5	0.73
ACCELERATOR MBTS	0.5	0.24
SULFUR	1.5	0.73
TOTAL	204.50	100.00

Properties	Method	Typical Value
Tc90 @160°C (Min)	ASTM D5289	16.1
Physical Properties (Cured @160°C/Tc90X2 Min)
300% Modulus (MPa)	ASTM D412	7.6
Tensile Strength (MPa)	ASTM D412	9.4
Elongation @ Break (%)	ASTM D412	386
Hardness (Shore A)	ASTM D2240	59
Oxygen Transmission Rate (Cured @160°C/Tc90X2 Min)
Permeation Rate (cc-mm/[m²-day])	ASTM D3985	255.0

NATURAL RUBBER/CHLOROBUTYL TUBE

Ingredient	PHR	%
ISNR 20	70.00	33.47
CHLOROBUTYL RUBBER IMPRAMER C1139	30.00	14.34
MAGNESIUM OXIDE	0.15	0.07
STEARIC ACID	2.00	0.96
ANTIOXIDANT TDQ	1.00	0.48
CARBON GPF N660	25.00	11.95
CALCIUM CARBONATE	60.00	28.69
PF RESIN	4.00	1.91
NAPHTHENIC OIL	10.00	4.78
PARAFFINIC WAX	1.00	0.48
ACCELERATOR CBS	0.4	0.19
ACCELERATOR TMTD	0.10	0.05
SULFUR	0.50	0.24
ACCELERATOR MBTS	1.50	0.72
ZINC OXIDE	3.50	1.67
TOTAL	209.15	100.00

Properties	Method	Typical Value
Tc90 @160°C for 30 min (min)	ASTM D5289	4.5
Physical Properties (Cured @160°C/Tc90X2 Min)
300% Modulus (MPa)	ASTM D412	3.2
Tensile Strength (MPa)	ASTM D412	12.0
Elongation @ Break (%)	ASTM D412	603
Hardness (Shore A)	ASTM D2240	42
Oxygen Transmission Rate (Cured @160°C/Tc90X2 Min)
Permeation Rate (cc-mm/[m²-day])	ASTM D3985	753.8

BUTYL/EPDM TUBE

Ingredient	PHR	%
BUTYL IMPRAMER R 1675	90.00	43.96
EPDM RUBBER (LOW ENB/40 MOONEY)	10.00	4.88
CARBON GPF N660	70.0	34.19
PARAFFINIC OIL	25.0	12.21
ZINC OXIDE	5.0	2.44
STEARIC ACID	1.0	0.49
ACCELERATOR TMTD	1.8	0.85
ACCELERATOR MBTS	0.5	0.24
SULFUR	1.5	0.73
TOTAL	204.75	100.00

Properties	Method	Typical Value
Tc90 @160°C for 40 min (min)	ASTM D5289	13.8
Physical Properties (Cured @160°C/Tc90X2 Min)
300% Modulus (MPa)	ASTM D412	7.3
Tensile Strength (MPa)	ASTM D412	11.0
Elongation @ Break (%)	ASTM D412	442
Hardness (Shore A)	ASTM D2240	56
Oxygen Transmission Rate (Cured @160°C/Tc90X2 Min)
Permeation Rate (cc-mm/[m²-day])	ASTM D3985	336.0

Tyre Curing Bladder

Ingredient	PHR	%
BUTYL IMPRAMER R 1675	100.00	57.14
POLYCHLOROPRENE- LOW CRYSTALINITY	5.00	2.86
CARBON HAF N330	50.00	28.57
CASTOR OIL	5.00	2.86
STEARIC ACID	1.00	0.57
ZINC OXIDE	5.00	2.86
METHYLOL PHENOL CURING RESIN	9.00	5.14
TOTAL	175.00	100.00

Properties	Method	Typical Value
Tc90 @190°C (Min)	ASTM D5289	22.0
Physical Properties (Cured @190°C/Tc90+5 Min)
300% Modulus (MPa)	ASTM D412	4.7
Tensile Strength (MPa)	ASTM D412	14.0
Elongation @ Break (%)	ASTM D412	675
Hardness (Shore A)	ASTM D2240	56

Butyl Innertube- Bias Truck & Bus

Ingredient	PHR	%
BUTYL IMPRAMER R 1675	85.00	42.89
EPDM RUBBER (LOW ENB/40 MOONEY)	15.00	7.57
CARBON GPF N660	65.00	32.80
PARAFFINIC OIL	23.00	11.60
PHENOLIC RESIN	1.00	0.50
STEARIC ACID	1.00	0.50
ZINC OXIDE	5.00	2.52
ACCELERATOR TMT	1.50	0.76
ACCELERATOR MBTS	0.50	0.25
SULFUR	1.20	0.61
TOTAL	198.20	100.00

Properties	Method	Typical Value
Tc90 @160°C (Min)	ASTM D5289	17
Physical Properties (Cured @160°C/Tc90+3 Min)
300% Modulus (MPa)	ASTM D412	4.5
Tensile Strength (MPa)	ASTM D412	9.5
Elongation @ Break (%)	ASTM D412	550
Hardness (Shore A)	ASTM D2240	56

Butyl Innertube- Radial Application

Ingredient	PHR	%
BUTYL IMPRAMER R 1675	100.00	53.98
CARBON HAF N330	55.00	29.69
PARAFFINIC OIL	20.00	10.80
PHENOLIC RESIN	1.00	0.54
STEARIC ACID	1.00	0.54
ZINC OXIDE	5.00	2.70
ACCELERATOR TMT	1.50	0.81
ACCELERATOR MBTS	0.50	0.27
SULFUR	1.25	0.67
TOTAL	185.25	100.00

Properties	Method	Typical Value
Tc90 @160°C (Min)	ASTM D5289	22.0
Physical Properties (Cured @160°C/Tc90+3 Min)
300% Modulus (MPa)	ASTM D412	3.9
Tensile Strength (MPa)	ASTM D412	13.0
Elongation @ Break (%)	ASTM D412	700
Hardness (Shore A)	ASTM D2240	50

Butyl Innertube- Cycle

Ingredient	PHR	%
BUTYL IMPRAMER R 1675	85.00	41.82
EPDM RUBBER (LOW ENB/40 MOONEY)	10.00	4.92
BUTYL RECLAIM	10.00	4.92
CARBON GPF N660	65.00	31.98
PARAFFINIC OIL	23.00	11.32
PHENOLIC RESIN	1.00	0.49
STEARIC ACID	1.00	0.49
ZINC OXIDE	5.00	2.46
ACCELERATOR TMT	1.50	0.74
ACCELERATOR MBTS	0.50	0.25
SULFUR	1.25	0.62
TOTAL	203.25	100.00

Properties	Method	Typical Value
Tc90 @160°C (Min)	ASTM D5289	19.0
Physical Properties (Cured @160°C/Tc90+3 Min)
300% Modulus (MPa)	ASTM D412	5.2
Tensile Strength (MPa)	ASTM D412	8.5
Elongation @ Break (%)	ASTM D412	500
Hardness (Shore A)	ASTM D2240	58

Chlorobutyl Innertube

Ingredient	PHR	%
CHLOROBUTYL RUBBER IMPRAMER C1139	100.00	50.35
CARBON GPF N660	65.00	32.73
MAGNESIUM OXIDE	0.10	0.05
PARAFFINIC OIL	25.00	12.59
STEARIC ACID	1.00	0.50
ZINC OXIDE	5.00	2.52
ACCELERATOR TMT	1.00	0.50
ACCELERATOR MBTS	1.50	0.76
TOTAL	198.60	100.00

Properties	Method	Typical Value
Tc90 @160°C (Min)	ASTM D5289	8.0
Physical Properties (Cured @180°C/Tc90+3 Min)
300% Modulus (MPa)	ASTM D412	3.9
Tensile Strength (MPa)	ASTM D412	8.5
Elongation @ Break (%)	ASTM D412	600
Hardness (Shore A)	ASTM D2240	48

Web Formulary